The invention relates to a preparation method of load type desulfurizer, which comprises the following steps: activation of carrier; the active metal compound is dissolved in a solvent in the preparation of impregnating solution; the impregnation step 1 in activation after impregnation in step II obtained, filtering and drying to obtain load carrier active metal compound; the third step in the load active metal compound carrier impregnated with inorganic alkaline solution, filtering, drying, and product obtained after calcination desulfurizing agent. The desulfurizing agent obtained by the preparation method of the invention has the advantages of high dispersion of the active component and large load, thereby having a high desulfurization rate.
【技术实现步骤摘要】
本专利技术属于脱硫剂领域，特别是涉及一种用于脱除各种油品中硫化物的负 载型脱硫剂的制备方法。
技术介绍
近年来随着原油开采的不断进行，油品中硫含量呈逐年上升的趋势，人们 必须不断提高脱硫剂的脱硫能力才能满足进一步生产或加工的需要。现在制备 脱硫剂的方法主要包括捏合法和浸渍法两大类，较之采用纯机械捏合方法制备 脱硫剂的捏合法，浸渍法制备出的脱硫剂中活性组分具有更高的分散度。中国专利CN1609171公开了一种脱硫剂的制备方法，该脱硫剂以不同孔 结构的氧化铝混合物作为载体，先用含碱性助剂的水溶液浸渍氧化铝载体，干 燥、焙烧后再用含活性金属化合物的水溶液浸渍含碱性助剂的脱硫剂，再经千 燥、焙烧后得到脱硫剂成品。现有技术中存在的缺陷是1 )该现有技术中首先将碱性物质负载于载体上，再将含有碱性物质的载 体浸渍于含活性金属化合物的水溶液中，此时金属离子会与碱性物质生成水溶 性差的金属氢氧化物，这些物质附着于载体外表面并^f艮难再进入到载体的孔道 结构中，使得活性组分的分散度和负载量大大降低，导致硫容不高。2 )现有技术中，由于溶解性的限制，通常将活性金属化合物溶解于水中， ...
【技术保护点】
一种负载型脱硫剂的制备方法，包括以下步骤： ①载体的活化； ②将活性金属化合物溶解在溶剂中配制成浸渍液； ③将步骤①中活化后载体浸渍于步骤②中得到的所述浸渍液中，经过过滤、干燥后得到负载有活性金属化合物的载体； ④将 步骤③中得到所述负载有活性金属化合物的载体浸渍于无机碱性溶液中，经过过滤、干燥，再经过焙烧后得到脱硫剂成品。
【技术特征摘要】
【专利技术属性】
技术研发人员：夏道宏，张杰，项玉芝，徐斌，蒲延芳，闻学兵，
申请(专利权)人：北京三聚环保新材料股份有限公司，
类型：发明
国别省市：11[中国|北京]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。