The invention discloses a hydroxyl alumina nanoadjuvant based on the principle of chemical precipitation, a preparation method thereof and an accurate control method for its crystallinity. The method uses inorganic aluminium salts as precursors and alkaline solutions as precipitators to prepare nano-sized AlOOH adjuvants by chemical precipitation. The crystallinity of the final product can be precisely controlled by controlling the temperature and time in the reaction process. The method has simple operation process and good repeatability. The prepared AlOOH nanomaterials have uniform morphology, narrow particle size distribution and good stability, and have potential application prospects in biomedical fields such as vaccine adjuvants.
【技术实现步骤摘要】
一种结晶度可控的AlOOH纳米佐剂及其制备方法
本专利技术涉及AlOOH材料的制备方法，具体说是纳米AlOOH佐剂、其制备方法以及其结晶度的精确调控方法。
技术介绍
疫苗作为预防传染性疾病的重要武器，保留了病原菌刺激动物体免疫系统的特性，接种疫苗可以使集体获得针对病原体特异性的免疫力。疫苗佐剂作为一种可以非特异性增强或改变免疫应答类型的物质，是疫苗中的一种重要组分，尤其是一些减毒活疫苗和灭活疫苗，由于自身免疫原性的限制，需要加入佐剂才能发挥其免疫保护作用。铝盐作为疫苗佐剂已经有八十多年的历史，至今仍是应用最多的疫苗佐剂。而AlOOH作为铝盐佐剂中的重要一员，其佐剂效应与材料的物化特性直接相关。研究表明，AlOOH材料的结晶度是影响佐剂效应的重要因素，因此对AlOOH材料的制备和其结晶度的调控的具有重要意义。目前，在众多传统的AlOOH制备方法中，气相法、溶胶凝胶法、微乳液法等由于所需温度较高、仪器设备昂贵复杂、有机溶剂引入等原因，所得产物杂质不易分离，制备工艺较为复杂，在AlOOH结晶度的调控方面也缺乏系统的研究。因此，探索具有良好稳定性的AlOOH佐剂的制备工艺...
【技术保护点】
1.一种结晶度可控的AlOOH纳米佐剂的制备方法，包括以下步骤：1)取无机铝盐完全溶解于去离子水形成透明澄清的铝盐溶液；2)在上述铝盐溶液中均匀滴加碱性溶液，发生均匀沉淀并继续搅拌得混合液；3)对上述混合液进行水热反应；4)冷却、离心、洗涤、干燥得到最终的白色粉末固体。
【技术特征摘要】
1.一种结晶度可控的AlOOH纳米佐剂的制备方法，包括以下步骤：1)取无机铝盐完全溶解于去离子水形成透明澄清的铝盐溶液；2)在上述铝盐溶液中均匀滴加碱性溶液，发生均匀沉淀并继续搅拌得混合液；3)对上述混合液进行水热反应；4)冷却、离心、洗涤、干燥得到最终的白色粉末固体。2.根据权利要求1所述的一种结晶度可控的AlOOH纳米佐剂的制备方法，其特征在于：所述的铝盐包括硝酸铝、氯化铝、硫酸铝、异丙醇铝中的一种或其混合物。3.根据权利要求1所述的一种结晶度可控的AlOOH纳米佐剂的制备方法，其特征在于：步骤2)所述的沉淀剂是氢氧根离子沉淀剂。4.根据权利要求3所述的一种结晶度可控的AlOOH纳米佐剂的制备方法，其特征在于：所述的沉淀剂是乙二胺、氢氧化钠或氨水中的一种或其混合物。5.根据权利要求1所述的一种结晶度可控的AlOOH纳米佐剂的制备方法，其...
【专利技术属性】
技术研发人员：孙冰冰，梁智慧，郭幸娟，鱼歌，
申请(专利权)人：大连理工大学，
类型：发明
国别省市：辽宁,21