本发明专利技术公开了具有抗菌功能的塑料编织带，包括塑料编织带本体，该；该塑料编织带本体包括74％～99.5％的聚丙烯粒原料及碳酸钙粉及0.5％～10％的纳米银，0％～8％的香料，0％～8％的着色剂，该聚丙烯粒原料及碳酸钙粉相对密度是0.910～0.925，结晶度是55％～65％；本发明专利技术还公开了生产该具有抗菌功能的塑料编织带的生产工艺，用于沐浴洗刷的日用品场合。

Production process of plastic woven belt with antibacterial function

The invention discloses a plastic woven belt with antibacterial function, including a plastic braiding belt body, which comprises 74% to 99.5% polypropylene particles and calcium carbonate powder and 0.5% to 10% nano silver, 0% to 8% spices, 0% to 8% coloring agents, and the polypropylene grain raw material and calcium carbonate powder. The density is 0.910 ~ 0.925 and the crystallinity is 55% ~ 65%. The invention also discloses the production process of the plastic woven belt with antibacterial function, which is used in the daily necessities of bathing and washing.

【技术实现步骤摘要】
具有抗菌功能的塑料编织带的生产工艺
本专利技术涉及一种具有抗菌功能的塑料编织带的生产工艺。
技术介绍
现有技术中，塑料编织带用于编织塑料布或塑料编织袋，在人们日益追求将医疗保健与日常生活中的饮食起居融为一体的趋势下，如食疗、按摩保健治疗等项目层出不穷，塑料编织带应该赋予更多医疗保健的功能。
技术实现思路
本专利技术所要解决的技术问题是，提供一种生产具有抗菌功能的塑料编织带的生产工艺。本专利技术解决上述技术问题所采用的技术方案是：一种生产该具有抗菌功能的塑料编织带的生产工艺：A、准备主料及抗菌剂，所述主料包括聚丙烯胶粒及碳酸钙粉，所述碳酸钙粉和聚丙烯的质量比例为20：80至50：50，所述抗菌剂是纳米银：所述主料含量为74％～99.5％，所述抗菌剂的含量为0.5％～24％；将所述主料放进拌料槽中搅拌30s～120s，然后再取纳米银放进拌料槽中，共同搅拌5min～15min，拌料槽的温度为5℃～40℃；B、将步骤A中的主料及抗菌剂混合物放进拉膜机中进行加热300℃逐步融化，用内、外模具首先挤出膜状物料，并引入冷水槽进行冷却定形，所述膜状物料由牵引轮从所述冷水槽中引出，牵引进分割梳中进行分割形本文档来自技高网...

【技术保护点】
一种具有抗菌功能的塑料编织带的生产工艺，其特征在于：准备主料及抗菌剂，所述主料包括聚丙烯胶粒及碳酸钙粉，所述碳酸钙粉和聚丙烯的质量比例为20：80至50：50，所述抗菌剂是纳米银：所述主料含量为74％～99.5％，所述抗菌剂的含量为0.5％～24％；将所述主料放进拌料槽中搅拌30s～120s，然后再取纳米银放进拌料槽中，共同搅拌5min～15min，拌料槽的温度为5℃～40℃；B、将步骤A中的主料及抗菌剂混合物放进拉膜机中进行加热300℃逐步融化，用内、外模具首先挤出膜状物料，并引入冷水槽进行冷却定形，所述膜状物料由牵引轮从所述冷水槽中引出，牵引进分割梳中进行分割形成塑料编织带；C、将步骤B中...

【技术特征摘要】
1.一种具有抗菌功能的塑料编织带的生产工艺，其特征在于：准备主料及抗菌剂，所述主料包括聚丙烯胶粒及碳酸钙粉，所述碳酸钙粉和聚丙烯的质量比例为20：80至50：50，所述抗菌剂是纳米银：所述主料含量为74％～99.5％，所述抗菌剂的含量为0.5％～24％；将所述主料放进拌料槽中搅拌30s～120s，然后再取纳米银放进拌料槽中，共同搅拌5min～15min，拌料槽的温度为5℃～40℃；B、将步骤A中的主料及抗菌剂混合物放进拉膜机中进行加热300℃逐...