The invention discloses a methanol alkylation preparation method of p-xylene catalyst, Pt (ACAC) 2, Fe (ACAC) 2, Cu, BTC, tetrahydrofuran borane tetrahydrofuran complex, Cu (NO3) 2 - 3H2O and BTC as the main raw material in supercritical carbon dioxide fluid medium under the action of the super metal compounds critical as the precursor, Cu BTC porous material as a carrier, borane as reducing agent, reaction to obtain two yuan or multiple nano alloy catalysts supported on porous materials, the invention of p-xylene through alkylation with methanol, heterogeneous, and other steps to eliminate the traditional process, shorten the process, improve the yield of p-xylene.
【技术实现步骤摘要】
一种甲醇烷基化制取对二甲苯催化剂的制备方法
本专利技术涉及一种苯和甲醇烷基化高选择性制取对二甲苯的流化床催化剂及其制备方法,属于催化剂
技术介绍
对二甲苯是极为重要的大宗化工原料,主要用于生产对苯二甲酸和对苯二甲酸二甲醋。由于我国聚酯行业发展迅猛,带动了和消费量的增长,从而导致对二甲苯的消费量也快速增长。工业上一般是通过石油裂解产物进行芳烃分离、甲苯歧化或重芳烃烷基转移的方法生产对二甲苯,由于这些方法副产大量的苯,而苯的经济价值低,在一定程度上影响对二甲苯制备工艺的经济性。传统方法多采用固定床技术,床层温度不均匀,催化剂稳定性差、容易失活且不易再生为了提高催化剂稳定性,在反应过程中多需通入氢气作为载气,而氢气本身具有较高的价值,因此成本较高上；催化剂的制备和改性步骤繁琐,成本昂贵上述技术中苯的转化率多在30%一40%之间,原料利用率不够高。
技术实现思路
本专利技术的目的在于提供一种甲醇烷基化制取对二甲苯催化剂的制备方法，对二甲苯在二甲苯异构体中的选择性大幅度提高,省去了传统工艺中异构化等步骤,工艺路线缩短,对二甲苯单程收率大幅提高。一种甲醇烷基化制取对二甲...
【技术保护点】
一种甲醇烷基化制取对二甲苯催化剂的制备方法，其特征在于,该方法包括以下步骤：步骤1、将总质量为50mg的Pt（acac）2和Fe（acac）2前驱体放入体积为20ml的反应釜中,所述的Pt（acac）2和Fe（acac）2物质的量比为1:1；步骤2、将20g的Cu‑BTC纳米多孔材料放入反应釜中，然后加入500μL的四氢呋喃于反应釜中，封闭反应釜,压入150atm的超临界CO2于反应釜中,加热至60℃,并保温2h后,缓慢泄压,获得纳米多孔材料负载Pt与Fe前驱体的制备；步骤3、将上述前驱体放入反应釜中,加入1mL四氢呋喃硼烷, 封闭反应釜,压入150atm的超临界CO2于反...
【技术特征摘要】
1.一种甲醇烷基化制取对二甲苯催化剂的制备方法，其特征在于,该方法包括以下步骤：步骤1、将总质量为50mg的Pt（acac）2和Fe（acac）2前驱体放入体积为20ml的反应釜中,所述的Pt（acac）2和Fe（acac）2物质的量比为1:1；步骤2、将20g的Cu-BTC纳米多孔材料放入反应釜中，然后加入500μL的四氢呋喃于反应釜中，封闭反应釜,压入150atm的超临界CO2于反应釜中,加热至60℃,并保温2h后,缓慢泄压,获得纳米多孔材料负载Pt与Fe前驱体的制备；步骤3、将上述前驱体放入反应釜中,加入1mL四氢呋喃硼烷,封闭反应釜,压入150atm的超临界CO2于反应釜中,加热至80℃,并保温2h后,反应结束,自然冷却至室温后,缓慢泄压至常压；步骤4、连续压入80mL的超临界CO2于反应釜中,并以0.5ml/min的速率泄压,持续2h后停止,取出样品即可获得Cu-BTC负载...