The invention belongs to the technical field of alkylation reaction, in particular to a preparation method of an alkylation reaction catalyst for toluene and tertiary butyl alcohol, comprising the steps of preparing raw materials, mixing granules and drying products. Compared with the prior art, the invention has the following advantages: the invention takes into account paracresol structure multi electron active site, according to the charge distribution and the steric hindrance of preparing catalyst, the catalyst of long service life, can be used repeatedly, good activity, reaction time is shortened to 2 hours, calcination temperature reaches 600 DEG C, selectivity of tert butyl toluene reached 82.5%.
【技术实现步骤摘要】
一种甲苯与叔丁醇的烷基化反应催化剂的制备方法
本专利技术属于烷基化反应
,具体涉及一种甲苯与叔丁醇的烷基化反应催化剂的制备方法。
技术介绍
对叔丁基甲苯是一种重量的化工原料,是生产对叔丁基苯甲酸、对叔丁基苯乙醛、对叔丁基苯甲醚的中间体,也是香料、塑料、树脂工业中的重要中间体,生产对叔丁基甲苯的传统工艺采用的催化剂大多是液体酸,这些催化剂存在着催化剂与产品分离困难、排放大量废液、环境污染严重、难以持续生产等确定,沸石分子筛由于具有较高的催化活性和择形性,被广泛应用在甲苯的烷基化反应中,此时,甲苯转化率为39.6%,叔丁基甲苯的选择性为99.7%,对叔丁基甲苯的选择性为70%,其中对叔丁基甲苯的选择性较低,因此需要对其催化剂进一步研究,以提高其对叔丁基甲苯的选择性。
技术实现思路
本专利技术的目的是针对现有的问题,提供了一种甲苯与叔丁醇的烷基化反应催化剂的制备方法。本专利技术是通过以下技术方案实现的:一种甲苯与叔丁醇的烷基化反应催化剂的制备方法,包括以下内容:(1)原料准备,按重量份计,硅酮粉25份、对氨基苯磺酸40份、红辉沸石粉15份、环氧树脂20份;(2)将硅酮粉、红辉沸石粉在球磨机中球磨混合后,得到粒径为80-200μm的混合粉,在混合粉中加入环氧树脂和对氨基苯磺酸搅拌均匀,在120-140℃的条件下加热1.5-2小时,然后制成颗粒状,颗粒的直径为1.2-1.4cm;(3)将上述颗粒烘干至水分低于15%后,冷却包装即可。作为对上述方案的进一步改进,所述红辉沸石粉由硝酸银和硝酸钙改性沸石粉得到。作为对上述方案的进一步改进,所述硝酸银和硝酸钙的使用重量比为 ...
【技术保护点】
一种甲苯与叔丁醇的烷基化反应催化剂的制备方法,其特征在于,包括以下内容:(1)原料准备,按重量份计,硅酮粉25份、对氨基苯磺酸40份、红辉沸石粉15份、环氧树脂20份;(2)将硅酮粉、红辉沸石粉在球磨机中球磨混合后,得到粒径为80‑200μm的混合粉,在混合粉中加入环氧树脂和对氨基苯磺酸搅拌均匀,在120‑140℃的条件下加热1.5‑2小时,然后制成颗粒状,颗粒的直径为1.2‑1.4cm;(3)将上述颗粒烘干至水分低于15%后,冷却包装即可。
【技术特征摘要】
1.一种甲苯与叔丁醇的烷基化反应催化剂的制备方法,其特征在于,包括以下内容:(1)原料准备,按重量份计,硅酮粉25份、对氨基苯磺酸40份、红辉沸石粉15份、环氧树脂20份;(2)将硅酮粉、红辉沸石粉在球磨机中球磨混合后,得到粒径为80-200μm的混合粉,在混合粉中加入环氧树脂和对氨基苯磺酸搅拌均匀,在120-140℃的条件下加热1.5-2小时,然后制成颗粒状,颗粒的直径为1.2-1.4cm;(3)将上述颗粒烘...
【专利技术属性】
技术研发人员:程聚光,
申请(专利权)人:宣城市聚源精细化工有限公司,
类型:发明
国别省市:安徽,34