一种扁平片体粗粒无载体黑色砂制造技术

本实用新型专利技术属于化学染色料技术领域，具体涉及一种扁平片体粗粒无载体黑色砂。该扁平片体粗粒无载体黑色砂的颗粒为扁平片体结构，片体尺寸L满足1.00mm＜L＜6.00mm，片体厚度H满足1.00mm＜H＜2.00mm；并且，该扁平片体粗粒无载体黑色砂是经过抛光工艺和对辊研磨工艺加工而成的，颗粒表面光洁、圆润，无边棱，无坑槽，无毛刺；具有如此技术参数的扁平片体粗粒无载体黑色砂，整体比重为1.2～2g/m

A flat sheet coarse grained non Carrier Black Sand

The utility model belongs to the technical field of chemical dyeing material, in particular to a flat sheet coarse grained non carrier black sand. The flat sheet of coarse sand particles as the carrier free black flat sheet, sheet size L meet 1.00mm < L < 6.00mm, sheet thickness H meet 1.00mm < H < 2.00mm; and the flat sheet of coarse grain free carrier black sand is after polishing and formed of roller grinding process the particle surface is smooth, smooth, no edges, no pit, no burr; so the technical parameters of the flat sheet of coarse grain free carrier black sand, the overall proportion is 1.2 ~ 2g/m

【技术实现步骤摘要】
一种扁平片体粗粒无载体黑色砂
本技术属于化学染色料
，具体涉及一种扁平片体粗粒无载体黑色砂。
技术介绍
色砂通常由着色剂、载体、分散剂以及其他助剂组成，广泛用于生产出五颜六色的纤维、服装、日用塑料、电线及电缆、家用电器、农用薄膜、汽车配件、保健器械等制品。使用色砂具有以下优点：颜料分散良好，减少了着色工作量，色泽准确，降低设备清理费用；但现有色砂中，小颗粒色砂在用于染色过程中容易起尘，粉尘散发于空气中，被进行作业的人员吸入身体，对其健康造成影响，而大粒径色砂虽不易起尘，但存在分散性和流动性的不足的缺陷，且现有色砂通常为实心色砂，比重大，比表面积小，需要较长时间的高温条件才能完全熔化并发挥染色功能，这也使得其分散性、流动性和着色性都欠佳。
技术实现思路
基于以上缺陷，本技术提供一种颗粒尺寸大、比重小、比表面积大的扁平片体粗粒无载体黑色砂，其颗粒的尺寸为1.0mm～6.0mm，黑色砂整体比重为1.2～2g/m3，比表面积为350～420m2/g，可耐热200～400℃，熔融指数为0.8～2.2g/10min，在具有环保、浓度高、颜色黑等黑色砂通常具备的优点外，还具有不易起尘、流动性好、分散本文档来自技高网...

【技术保护点】
一种扁平片体粗粒无载体黑色砂，其特征在于：该扁平片体粗粒无载体黑色砂的颗粒为扁平片体结构，片体尺寸L满足1.00mm＜L＜6.00mm，片体厚度H满足1.00mm＜H＜2.00mm；并且，颗粒表面光洁、圆润，无边棱，无坑槽，无毛刺；颗粒内部为空心结构；其中片体尺寸L系指该扁平片体粗粒无载体黑色砂的颗粒在各个方向上的最大尺寸。

【技术特征摘要】
1.一种扁平片体粗粒无载体黑色砂，其特征在于：该扁平片体粗粒无载体黑色砂的颗粒为扁平片体结构，片体尺寸L满足1.00mm＜L＜6.00mm，片体厚度H满足1.00mm＜H＜2.00mm；并且，颗粒表面光洁、圆润，无边棱，无坑槽，无毛刺；颗粒内部为空心结构；其中片体尺寸L系指该扁平片体粗粒无载体黑色砂的颗粒在各个方向上的最大尺寸。2.根据权利要求1所述的扁平片体粗粒无载体黑色砂，其特征在于：该扁平片体粗粒无载体黑色砂的比重为1.2～2g/m3，比表面积为350～420m2/g，耐热范围为200～400℃，熔融指数为0.8～2.2g/10min。3.根据权利要求1所述的...