The invention discloses a method for chlorobenzene low-temperature catalytic combustion catalyst and its preparation method and application of the catalyst is mainly composed of Ce doped TiO2 as carrier and supported ruthenium oxide or vanadium oxide, wherein Ce and Ti atomic ratio is 2:8~4:6, RuO2 or V2O5 accounted for by the oxide carrier weight percentage, load RuO2 for 0.5%~2% or V2O5. The carrier was prepared by solvent evaporation and self-assembly, and the active component was introduced by impregnation. The preparation method of the catalyst is simple, and no waste liquid is generated. The catalyst has high activity, less by-products and good stability for the catalytic combustion of chlorobenzene, and is especially suitable for low temperature catalytic combustion to eliminate chlorinated volatile organic compounds.
【技术实现步骤摘要】
用于氯苯低温催化燃烧的催化剂及其制备方法和应用
本专利技术属于催化环保
，特别涉及一种用于氯苯低温催化燃烧的催化剂及其制备方法和应用。
技术介绍
含氯挥发性有机化合物CVOCs（ChlorinatedVolatileOrganicCompounds）和许多基质材料兼容，在工业上具有广泛的用途，是VOCs中的一类。其中氯代芳香烃类污染物主要来自于工业生产过程泄漏和排放及城市垃圾焚烧或火电厂废气中，其化学性质稳定，会在生物体内蓄积，危害很大。主要危害包括抑制神经中枢，损害肝脏和肾脏。由于上述产生污染物的过程都是涉及到现阶段国计民生的工业，大量含氯化合物的排放是不可避免的。因此，目前还不具备从源头上消除含氯易挥发性烃类所造成的污染可能性。而采取后处理的方法消除氯代芳香烃污染物最有效的方法之一。近几年来，对于挥发性有机化合物(VOCs)的综合治理受到了越来越广泛的关注。目前，对于含氯挥发性有机物的去除，主要包括物理方法和化学方法两大类技术。物理方法主要包括：活性吸附法、吸收除气法、冷凝收集法和生物处理方法。化学方法主要包括：催化加氢脱氯法、光催化降解法和催化燃烧法。...
【技术保护点】
一种用于氯苯低温催化燃烧的催化剂，其特征在于，该催化剂是以Ce掺杂的TiO2作为载体及其负载的氧化钌或氧化钒构成，其中Ce与Ti的原子比为2:8~4:6，以氧化物RuO2或V2O5占载体的重量百分数计，RuO2或V2O5的负载量为0.5%~2%。
【技术特征摘要】
1.一种用于氯苯低温催化燃烧的催化剂，其特征在于，该催化剂是以Ce掺杂的TiO2作为载体及其负载的氧化钌或氧化钒构成，其中Ce与Ti的原子比为2:8~4:6，以氧化物RuO2或V2O5占载体的重量百分数计，RuO2或V2O5的负载量为0.5%~2%。2.一种根据权利要求1所述的用于氯苯低温催化燃烧催化剂的制备方法，其特征在于，具体包括以下步骤：（1）载体的制备第一步：以六水合硝酸铈为铈前驱体，配制0.25mol/L的硝酸铈乙醇溶液；第二步：以异丙醇钛为钛的前驱体，配制0.25mol/L的异丙醇钛乙醇溶液；第三步：按照Ce与Ti的原子比为2:8~4:6，量取一定体积的硝酸铈乙醇溶液和异丙醇钛乙醇溶液；第四步：将水浴锅置于通风橱中，在40~60oC水浴的条件下，将硝酸铈乙醇溶液逐滴加入到异丙醇钛乙醇溶液中；第五步：计算所加入的异丙醇钛水解需...
【专利技术属性】
技术研发人员：何丹农，蔡婷，袁静，赵昆峰，金彩虹，
申请(专利权)人：上海纳米技术及应用国家工程研究中心有限公司，
类型：发明
国别省市：上海,31