A kind of honeycomb body and its preparation process for the regenerative catalysis of organic waste gas with rare-earth based integral molding type. The purpose of the invention is to combine the rare earth active component and the regenerative ceramic substrate evenly and integrate molding together with the technology of regenerative ceramic and catalytic oxidation, and provide a catalyst for simultaneous heat storage and catalysis to be applied to the treatment of organic waste gas at present. The preparation method of the invention is to uniformly mix the active component precursor and cordierite, add other organic auxiliaries, mix and form, and form the catalyst through extrusion, drying and roasting.
【技术实现步骤摘要】
一种稀土基整体成型式有机废气蓄热催化用蜂窝体及其制备工艺
本专利技术涉及环保
，特别是一种VOC有机废气蓄热催化用含有稀土基活性成分的催化剂及其制造方法。技术背景VOC是挥发性有机化合物(VolatileOrganicCompounds)的英文缩写，是指在室温下饱和蒸气压大于70.91Pa，常压下沸点小于260℃的有机化合物。从环境监测的角度来讲，指以氢火焰离子检测器检出的非甲烷总烃类检出物的总称，主要包括烷烃类、芳烃类、烯烃类、卤烃类、酯类、醛类、酮类和其他有机化合物。随着工业化进程的快速发展，化工、电子、印刷、喷漆等行业无组织排放的VOC废气量不断增大，对于当前大气环境以及人类健康造成了极大的危害。传统的VOC处理方法有非破坏性方法、破坏性方法和两者的联合方法。非破坏性方法即回収法，主要有炭吸附、变压吸附、吸收法、冷凝法及膜分离技术：一般是通过物理方法，改变温度、压力或采用选择性吸附剂和选择性渗透膜等方法来富集分离VOC；破坏性方法有直接燃烧、热氧化、催化燃烧、生物氧化、等离子体法、紫外光催化氧化法及其集成技术：主要是通过化学或生化反应，用热、光、催...
【技术保护点】
一种稀土基整体成型式有机废气蓄热催化用蜂窝体及其制备工艺，其特征是该催化剂由以下组分：焦宝石、刚玉、氧化铝、高岭土、堇青石、纳米二氧化钛、硝酸铈、偏钒酸铵、有机助剂经过泥料混炼、陈腐、整体挤出成型、干燥、切割、窑炉烧成等工序制备而成；所述组分中：焦宝石30‑40份，刚玉为10‑15份，氧化铝微粉5‑12份，高岭土10‑15份，纳米二氧化钛10‑13份，硝酸铈5‑8份，偏钒酸铵1‑3份，有机助剂3.5‑10份。
【技术特征摘要】
1.一种稀土基整体成型式有机废气蓄热催化用蜂窝体及其制备工艺，其特征是该催化剂由以下组分：焦宝石、刚玉、氧化铝、高岭土、堇青石、纳米二氧化钛、硝酸铈、偏钒酸铵、有机助剂经过泥料混炼、陈腐、整体挤出成型、干燥、切割、窑炉烧成等工序制备而成；所述组分中：焦宝石30-40份，刚玉为10-15份，氧化铝微粉5-12份，高岭土10-15份，纳米二氧化钛10-13份，硝酸铈5-8份，偏钒酸铵1-3份，有机助剂3.5-10份。2.根据权利要求1所述一种稀土基整体成型式有机废气蓄热催化用蜂窝体及其制备工艺，所述有机助剂为纤维素、脂肪酸，所述纤维素：脂肪为1：（3-6）。3.一种稀土基整体成型式有机废气蓄热催化用蜂窝体的制造方法：用一定量的粉料和一定量的有机助剂混合，加入适量的去离子水，捏合均匀，陈腐一段时间后，成型挤出相应要求规格的催化剂，催化剂湿胚干燥定型、切割，在经过窑炉烧成制得催化剂。4.根据权利要求4所述的一种稀土基整体成型式有机废气蓄热催化用蜂窝体的制造方法...
【专利技术属性】
技术研发人员：吴道君，李军营，杨晓波，陈浩，
申请(专利权)人：湖北神雾热能技术有限公司，
类型：发明
国别省市：湖北,42