Low vanadium catalyst of the invention discloses a sol prepared by pyromellitic acid two four anhydride, including main catalyst and catalyst, the main catalyst for V2O5 and TiO2, V:Ti molar ratio of 1:0.1 to 1:5; B2O3, SnO2, catalyst for CeO2 and Sb2O3 to V, the amount of substance is the benchmark of 1, B the amount of substance is 0.001 ~ 0.1 Sn, the amount of substance is 0.001 ~ 0.1 Ce, the amount of substance is 0.001 ~ 0.1 Sb, the amount of substance is 0.001 ~ 0.1. The method used in the invention is simple and has wide raw materials, and it can prepare large amount of catalyst with fine particle size, good selectivity and low vanadium content. It is suitable for the application of gas phase oxidation of four toluene.
【技术实现步骤摘要】
溶胶-烧结法制备均酐的低钒催化剂
本专利技术涉及化学
，具体涉及一种催化剂及其制备方法，尤其是溶胶-烧结法制取低钒催化剂用于气相氧化法制备均酐。
技术介绍
目前，均酐的制备方法主要有三种，分别为均四甲苯氧化法、偏三甲苯烷基化法和一氧化碳法。其中工业上使用较为广泛的是均四甲苯气相氧化法，其优点是只需一步即可制得均酐，工艺简单；均四甲苯成本较低且以空气为氧化剂，可以连续制备，便于工业生产。制备均酐催化剂的常用制备工艺有喷涂法、浸渍法等。一般对均酐催化剂的制备采用喷涂法，以预定比例将各组分混合制成悬浮液备用，然后用喷枪将悬浮液喷涂至载体表面形成一定厚度，最后焙烧活化催化剂。通过水热法控制反应条件，可以得到尺寸均一可控的纳米粒子，而纳米粒子的粒度则会影响催化剂催化性能。水热法是指在高温高压的密闭容器中，以水作为介质进行的化学反应。而微波水热法是将传统的水热法与微波结合在一起，具有加热速度快，反应灵敏，受热体系均匀等特点，使其能快速制备出粒径分布窄、形态均一的纳米粒子。目前，工业上采用的催化剂是以V2O5-TiO2为主，其他氧化物为辅的复合催化剂，但由于制取的催化剂颗...
【技术保护点】
一种溶胶‑烧结法制备均酐的低钒催化剂，其特征在于，包括主催化剂和助催化剂，所述主催化剂为V2O5和TiO2，V：Ti摩尔比为1：0.1～1：5；助催化剂为B2O3、SnO2、CeO2和Sb2O3，以V的物质的量基准为1，则B的物质的量为0.001～0.1，Sn的物质的量为0.001～0.1，Ce的物质的量为0.001～0.1，Sb的物质的量为0.001～0.1。
【技术特征摘要】
1.一种溶胶-烧结法制备均酐的低钒催化剂，其特征在于，包括主催化剂和助催化剂，所述主催化剂为V2O5和TiO2，V：Ti摩尔比为1：0.1～1：5；助催化剂为B2O3、SnO2、CeO2和Sb2O3，以V的物质的量基准为1，则B的物质的量为0.001～0.1，Sn的物质的量为0.001～0.1，Ce的物质的量为0.001～0.1，Sb的物质的量为0.001～0....
【专利技术属性】
技术研发人员：王旭红，柴文，惠洋，殷仕龙，王哲飞，余磊，
申请(专利权)人：常熟理工学院，
类型：发明
国别省市：江苏,32