一种以凹凸棒石为载体的脱硝催化剂及其制备方法技术

本发明专利技术公开了一种以凹凸棒石为载体的脱硝催化剂及其制备方法，该脱硝催化剂包括凹凸棒石、MoO2、Cr2O3、MnO2及SnO2；制法包括：将MoO2、Cr2O3、MnO2及SnO2混匀后，加入凹凸棒石载体，浸渍，制得脱硝催化剂浆料，经干燥，焙烧后，即可。优点为该脱硝催化剂具有较低的起活温度、脱硝效率高；同时，该制法简单，可操作性强，降低了生产成本。

A catalyst for denitrification with attapulgite as carrier and its preparation method

The invention discloses a denitration catalyst carrier and preparation method thereof using attapulgite as the denitration catalyst, including attapulgite, MoO2, Cr2O3, MnO2 and SnO2; the preparation method comprises: MoO2, Cr2O3, MnO2 and SnO2 after mixing, adding attapulgite carrier, impregnated, prepared denitration catalyst slurry, drying, roasting, can. The advantage is that the denitrification catalyst has low living temperature and high denitrification efficiency. At the same time, this method is simple, easy to operate, and reduces the production cost.

【技术实现步骤摘要】
一种以凹凸棒石为载体的脱硝催化剂及其制备方法
本专利技术属于催化剂领域，尤其涉及一种以凹凸棒石为载体的脱硝催化剂及其制备方法。
技术介绍
现有的SCR脱硝催化剂中，以V2O5为活性组分，TiO2为载体的钒钛系脱硝催化剂工业应用程度最高。现已有众多的钒钛系脱硝催化剂的制备方法及脱硝工艺在本领域公开，如记载在申请号或者专利号为CN101829560B、CN103240078B、CN101791518B、CN102989484等专利技术中。而在我国燃煤电厂的实际工况中，由于烟气成分复杂、温度变化大、对脱硝催化剂的活性、热稳定性以及寿命都有着较高的要求，同时，又由于传统的锐钛矿型TiO2载体存在比表面积较小、传质效率较低以及在高温的烟气环境中容易烧结，转化成为金红石相等缺点，因此，对TiO2的进一步改进，以制备脱硝效率更高、稳定性更好的脱硝催化剂成为热潮，其中，以氧化物、分子筛等材料与TiO2组成的复合载体，是一种有效地改进TiO2物理化学性质的方法，而目前在SCR脱硝领域，对复合载体的研究和应用也逐渐深入。
技术实现思路
本专利技术的第一目的是提供一种脱硝效率高且热稳定性、水热稳定性强的以凹凸本文档来自技高网...

【技术保护点】
一种以凹凸棒石为载体的脱硝催化剂，其特征在于按重量份计包括如下原料：凹凸棒石70‑100份、MoO2 40‑60份、Cr2O3 32‑56份、MnO2 7‑15份及SnO29‑22份。

【技术特征摘要】
1.一种以凹凸棒石为载体的脱硝催化剂，其特征在于按重量份计包括如下原料：凹凸棒石70-100份、MoO240-60份、Cr2O332-56份、MnO27-15份及SnO29-22份。2.根据权利要求1所述的以凹凸棒石为载体的脱硝催化剂，其特征在于：所述凹凸棒石的重量份数为80-90份。3.根据权利要求1所述的以凹凸棒石为载体的脱硝催化剂，其特征在于：所述MoO2的重量份数为45-55份。4.根据权...

【专利技术属性】
技术研发人员：周丽，
申请(专利权)人：周丽，
类型：发明
国别省市：江苏,32