一种防腐自修复涂料制造技术
A self repair coating for anticorrosion
The invention discloses a self repairing anticorrosive paint and preparation method thereof, the invention of the self repairing coating corrosion percentage by mass with self repairing component 5 10%, the self repairing coating containing antirust paint filler. The self repairing component can be a loaded microsphere with a load release agent, and the load of the inhibitor is 10 ~ 30% of the mass of the microspheres. Self repairing anticorrosive coating prepared by the invention, the coating corrosion damage, automatic release of inhibitors, the barrier metal contact with the corrosive medium, so as to prevent further corrosion effect, and its high sensitivity, strong corrosion resistance, the preparation method is simple and easy to control, no pollution, low cost, suitable for industrial production.
【技术实现步骤摘要】
一种防腐自修复涂料
本专利技术属于金属防腐涂料领域，涉及一种能够长期有效抑制金属或其他腐蚀的防腐自修复涂料及其制备方法。
技术介绍
全世界每年因金属腐蚀造成的直接经济损失约达7000亿美元，我国因金属腐蚀造成的经济损失巨大，占国民生产总值(GNP)的3％，因而，金属材料的腐蚀与防护一直是人们研究的重点。为了减缓和阻止金属腐蚀反应，延长金属产品的生命周期，金属设备在制造过程中通常需在其表面添加防腐涂层。该技术既能保持金属材料原有的物理、力学性能，又具有良好的防腐效果和较高的经济效益。但简单隔离金属表面与腐蚀介质的防腐涂层属于“被动”防腐体系，功能单一，且在涂层受侵蚀时，金属基材亦会引发严重的腐蚀。为解决此问题，研究者在防腐涂层中掺入磷酸锌作为缓蚀剂(CN102352172A，2011)，当腐蚀介质渗入涂层时，磷酸锌通过在金属表面形成保护膜而起到阴极保护的作用。同时亦有其他研究者公开一种在环氧有机涂层中添加钼酸盐掺杂聚吡咯作为缓蚀剂(CN105001759A，2015)，也表现出优秀的腐蚀抑制效果。但是，缓蚀剂一般需要达到一定溶解度才能发挥效应保护金属，而过高的溶解度...
【技术保护点】
一种防腐自修复涂料，其特征在于，所述防腐自修复涂料按质量百分比含有自修复组分5‑10％，所述自修复涂料为含有防锈填料的涂料。
【技术特征摘要】
1.一种防腐自修复涂料，其特征在于，所述防腐自修复涂料按质量百分比含有自修复组分5-10％，所述自修复涂料为含有防锈填料的涂料。2.根据权利要求1所述的防腐自修复涂料，其特征在于，所述自修复涂料还含有聚合物。3.根据权利要求1或2所述的防腐自修复涂料，其特征在于，所述自修复涂料还含有固化剂。4.根据权利要求1所述的防腐自修复涂料，其特征在于，所述自修复组分为负载缓释剂的微球，缓蚀剂负载量为微球质量的10～30％。5.根据权利要求4所述的防腐自修复涂料，其特征在于，所述微球为pH响应型纳米微球，所述pH响应型纳米微球在pH为6-10时释...
【专利技术属性】
技术研发人员：李国良，杨硕，王军鹏，周士乐，齐涛，
申请(专利权)人：中国科学院过程工程研究所，
类型：发明
国别省市：北京,11
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。