The invention discloses a low-temperature waterborne anticorrosive coatings for metal, which comprises the following components in parts by weight: 10 15 poly ortho toluene glycidyl ether, 15 20 copies of the bisphenol F epoxy resin, 10 20 poly phenyl glycidyl ether, 20 silica sol, 30 copies of the 3 10 color pigments, 1 5 curing agent, 30 to 60 parts water, 6 10 two, 8 10 butyl salicylic acid, 1 6 copies, 1.6 copies of 0.6 propiconazole chromium oxide green, 15 20 benzoic acid, 30 60 styrene acrylic emulsion. In the invention, the paint film performance, film strength is high, and the utility of the waterborne epoxy resin coatings with natural pollution-free natural corrosion inhibitor, corrosion inhibitor coatings and waterborne anti-corrosive special emulsion combined with good corrosion resistance, waterborne anticorrosive coatings is superior to the traditional.
【技术实现步骤摘要】
低温水性防腐金属涂料
本专利技术涉及一种水性涂料，具体涉及低温水性防腐金属涂料。
技术介绍
随着现代工业的飞速发展，金属表面的防腐越来越受到各行各业的高度重视，采用涂料涂覆防腐是一种既经济又有效的方法。对工矿企业来说，金属腐蚀造成了经济上的巨大损失是难以估量的，约占全球钢产量的15％-20％，可见，对腐蚀的防护是何等的重要。防止金属腐蚀的方法有很多，如采用电镀和阴极保护，造成了排放污染，不利于环境保护；还有在使用耐腐蚀合金，虽起到防腐作用，但工程造价达。经过实践证明，采取涂料层防护是最有效、最经济普遍的方法。目前金属涂料大多含有有机溶剂，在涂装过程中极容易挥发，严重污染了大气，破坏了生态环境，如今环境保护越来越受到重视，水性金属涂料必将取代传统的溶剂型涂料，将成为未来防腐涂料的主流，水性环氧涂料对金属的着力好收缩率低，但总的来说水性金属涂料的防腐性能、附着力与油性环氧涂料还有相当的差距。
技术实现思路
本专利技术所要解决的技术问题是水性金属涂料防腐性能差，目的在于提供低温水性防腐金属涂料，解决水性金属涂料防腐蚀的问题。本专利技术通过下述技术方案实现：低温水性防腐金属涂...
【技术保护点】
低温水性防腐金属涂料，其特征在于，包括以下重量份数的组分：10‑15份的聚邻甲苯缩水甘油醚、15‑20份的双酚F型环氧树脂、10‑20份的聚苯基缩水甘油醚、20‑30份的硅溶胶、3‑10份着色颜料、1‑5份固化剂，30‑60份水、6‑10份二丁脂、8‑10份水杨酸、1‑6份丙环唑、0.6‑1.6份氧化铬绿、15‑20份苯甲酸、30‑60份的苯丙乳液。
【技术特征摘要】
1.低温水性防腐金属涂料，其特征在于，包括以下重量份数的组分：10-15份的聚邻甲苯缩水甘油醚、15-20份的双酚F型环氧树脂、10-20份的聚苯基缩水甘油醚、20-30份的硅溶胶、3-10份着色颜料、1-5份固化剂，30-60份水、6-10份二丁脂、8-10份水杨酸、1-6份丙环唑、0.6-1.6份氧化铬绿、15-20份苯甲酸、30-60份的苯丙乳液。2.根据权利要求1所述的低温水性防腐金属涂料，其特征在于，还包括以下重量份数的组分：0.1-1份分散剂、0.1-1份消泡剂、1-5份成膜助剂、0.2-0.8份抗...
【专利技术属性】
技术研发人员：钟华军，柏建波，吴继忠，
申请(专利权)人：德阳森华新材料科技有限公司，
类型：发明
国别省市：四川,51