The invention discloses a wind resistant heavy-duty wind power equipment of water metal coating, coating composition including acrylic emulsion, deionized water, silicone resin, polyimide, vinyl resin, nanometer size, composite anticorrosion pigment dispersant, wetting agent, defoaming agent, curing agent, film-forming agent. The invention is very high and low temperature performance of polyimide resin, highly corrosion resistant silicone resin; weather resistance, wind power, insulation; nanometer size nano titanium dioxide, greatly enhance the wear resistance, sand properties; product is non-toxic, environmental protection, and is suitable for wind power equipment of wind resistant and corrosion.
【技术实现步骤摘要】
耐风沙重防腐风电设备水性金属涂料
本专利技术涉及水性涂料领域,具体涉及一种耐风沙重防腐风电设备水性金属涂料。
技术介绍
风力发电成为了近几年发挥在那最为迅速的可再生资源,开始从“补充源”朝向“战略替代能源”的方向发展。疯了发电站长期暴露在恶劣的气候环境中,需要进行有效的防腐保护;其中大型风电设备的设备昂贵,工作环境恶劣,现场不便对设备进行拆卸维修。塔架的防腐工作便成为保证风力发电的重要部分,因此为延长塔架寿命的涂装极其重要。随着国内风电产业的蓬勃发展,而风电产业的特殊环境对于涂料的性能要求就变得极为严格。目前运行中的风电设备涂料大多源自进口,成本高且实际运行效果并不理想;因此在风电设备涂料的研究与开发方面,降低成本和性能改进显得尤为迫切。
技术实现思路
针对上述问题,本专利技术提供了一种耐风沙重防腐风电设备水性金属涂料。本专利技术采取的技术方案是:一种耐风沙重防腐风电设备水性金属涂料,按质量分数包括丙烯酸乳液46份去离子水29份有机硅树脂22份聚酰亚胺18份乙烯树脂18份纳米浆料10份复合防腐颜料2份分散剂0.3份润湿剂0.5份消泡剂0.4份固化剂0.4份成膜助剂0.2份。作为一种优选的技术方案:所述的有机硅树脂为SN480或SN600。作为一种优选的技术方案:所述的纳米浆料为为纳米二氧化钛。作为一种优选的技术方案:复合防腐颜料优选为复合铁钛粉。作为一种优选的技术方案:所述的分散剂为SN5040、CY540中的一种或两种。作为一种优选的技术方案:所述的润湿剂为PE100和H436中的一种或两种。作为一种优选的技术方案:所述的消泡剂为SPA202和D160中的一 ...
【技术保护点】
一种耐风沙重防腐风电设备水性金属涂料,其特征在于:耐风沙重防腐风电设备水性金属涂料按质量分数包括丙烯酸乳液 46份去离子水 29份有机硅树脂 22份聚酰亚胺 18份乙烯树脂 18份纳米浆料 10份复合防腐颜料 2份分散剂 0.3份润湿剂 0.5份消泡剂 0.4份固化剂 0.4份成膜助剂 0.2份。
【技术特征摘要】
1.一种耐风沙重防腐风电设备水性金属涂料,其特征在于:耐风沙重防腐风电设备水性金属涂料按质量分数包括丙烯酸乳液46份去离子水29份有机硅树脂22份聚酰亚胺18份乙烯树脂18份纳米浆料10份复合防腐颜料2份分散剂0.3份润湿剂0.5份消泡剂0.4份固化剂0.4份成膜助剂0.2份。2.根据权利要求1所述的一种耐风沙重防腐风电设备水性金属涂料,其特征在于:所述的有机硅树脂为SN480或SN600。3.根据权利要求1所述的一种耐风沙重防腐风电设备水性金属涂料,其特征在于:所述的纳米浆料为为纳米二氧化钛。4.根据权利要求1所述的一种耐风沙重防腐风电设备水性金属涂料,其特征在于:复合防腐颜料优选为复合铁钛粉。5....