The invention discloses a heavy steel structure anticorrosion waterborne metallic coatings, coating composition including acrylic resin, amino resin, nano zirconium phosphate, deionized water, filler, chloroprene rubber adhesive, metal powder, dispersant, wetting agent, defoaming agent, curing agent, antiseptic, pigment. The invention of chloroprene rubber adhesive compound acrylic resin and amino resin coating itself has good flame retardancy; functional nano materials nanometer zirconium phosphate flame retardant, improve the foaming rate, and water corrosion: Fungicides effectively improve the antiseptic effect of the coating of the product; the product is non-toxic, ring, has good market foreground, suitable promotion.
【技术实现步骤摘要】
重防腐钢结构水性金属涂料
本专利技术涉及水性涂料领域,具体涉及一种重防腐钢结构水性金属涂料。
技术介绍
钢结构作为一种绿色节能环保材料,已被广泛应用于建筑中,但是裸露钢结构具有两大安全隐患:易腐蚀和低耐火性。当钢材的受热温度升高到500℃以上时,会因强度下降而失去支撑力。同时,钢结构在空气和潮湿的环境中易于腐蚀,腐蚀严重时,钢结构强度下降。因此,钢结构在发生火灾和腐蚀时,往往会导致建筑物垮塌,造成较大的人员伤亡和巨大的经济损失。所以必须对钢结构进行防火防腐保护,以保障其安全性。在钢结构表面涂敷涂料是众多钢结构防护措施中最为经济有效的方法。从现有钢结构涂料来看,大多数涂料功能比较单一,防腐涂料不妨火,而防火涂料不防腐,往往需要多道涂装施工即底涂防腐涂料再涂防火涂料,工艺繁琐,施工工期长,成本高,而且一旦防腐涂料与底材剥离,防火涂料也即脱落失效。钢结构涂料是众多涂料中的一种,它适用于污水、海水、工业水、输油、输气等管线以及桥梁、电力设备、网架及各类化工设备防腐蚀的保护,具有广泛的应用前景。但是,用现有的钢结构涂料完成外壁涂覆的钢结构在运输过程中,因为要经过吊装、汽运,或者是装船、海运等过程,会受到不同程度的碰撞、损坏,因此,目前大部分的涂覆钢结构在到达目的地后都需要进行补涂或复涂,这不仅浪费了大量的人力和物力,提高了造价,还会影响施工的进度。目前国内外已有的钢结构涂料按照材料形态可分为:水基型、溶剂型和粉末型;按照防火机理钢结构防火涂料又可分为膨胀型和非膨胀型。随着人们节能环保意识的增强,水性超薄膨胀型钢结构涂料因其既能满足环保要求,又具有较好的防火性能,成为 ...
【技术保护点】
一种重防腐钢结构水性金属涂料,其特征在于:重防腐钢结构水性金属涂料的成分按质量份包括丙烯酸树脂 40份纳米磷酸锆 26份去离子水 26 份填料 25份金属粉 15份氯丁橡胶粘合剂 5份氨基树脂 3份体质颜料 3份杀菌剂 1份润湿剂 0.5份消泡剂 0.4份固化剂 0.4 份分散剂 0.2份。
【技术特征摘要】
1.一种重防腐钢结构水性金属涂料,其特征在于:重防腐钢结构水性金属涂料的成分按质量份包括丙烯酸树脂40份纳米磷酸锆26份去离子水26份填料25份金属粉15份氯丁橡胶粘合剂5份氨基树脂3份体质颜料3份杀菌剂1份润湿剂0.5份消泡剂0.4份固化剂0.4份分散剂0.2份。2.根据权利要求1所述的一种重防腐钢结构水性金属涂料,其特征在于:所述体质颜料为二氧化硅或碳酸钙。3.根据权利要求1所述的一种重防腐钢结构水性金属涂料,其特征在于:所述固化剂为酚醛改性胺。4.根据权利要求1所述的一种重防腐钢结构水性金属涂料,其特征在于:所述的填料为六钛酸钾晶须或改性纳米蒙脱土中的一种或两种。5....
【专利技术属性】
技术研发人员:金勇云,王隆经,
申请(专利权)人:沈阳宣伯新材料科技有限公司,
类型:发明
国别省市:辽宁,21
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。