The present invention relates to the technical field of waterborne coatings, especially the technical field of matte paint, in particular discloses a matte finishing varnish, which comprises the following components: the quality of water-based acrylic emulsion matte 50 ~ 60, 30 ~ 46 copies of deionized water, wetting agent 0.05 ~ 0.1, defoaming agent 0.1 ~ 0.2, 1 ~ 2 propylene glycol, coalescents 1 ~ 2, 0.2 ~ 0.4 thickener. The present invention matte finishing varnish has the advantages of high gloss and good dispersion, easy to form a layered and precipitation, storage stability, to avoid the use of easy moldy, white powder dumb questions.
【技术实现步骤摘要】
一种哑光罩面清漆
本专利技术涉及水性涂料
,尤其是哑光漆
技术介绍
哑光罩面清漆可以起到保护底材涂料(水包水多彩涂料,真石漆,质感涂料等)的作用,同时提高底材涂料的性能,如耐水性,耐沾污性,耐擦洗性等。但是目前我国大部分哑光罩面清漆还是主要以哑粉消光为主,即涂料中以哑粉作为消光剂,其添加量在1~1.5%左右。哑粉主要成分为二氧化硅,添加量在0.5~1%时储存易在涂料中形成沉淀。施工中,为避免储存分层必须将黏度提高,从而导致了施工用量过大。此外,哑粉和丙烯酸乳液混合干燥后易发霉、发白,影响涂层的外观。
技术实现思路
本专利技术要解决的技术问题是提供一种哑光罩面清漆,具有光泽好和分散性好的优点,不易形成分层和沉淀,储存稳定,避免了使用哑粉易发霉、发白的问题。为解决上述技术问题,本专利技术所采取的技术方案是:一种哑光罩面清漆,包括如下质量份数的组分:水性丙烯酸哑光乳液50~60份,去离子水30~46份,基材润湿剂0.05~0.1份,消泡剂0.1~0.2份,丙二醇1~2份,成膜助剂1~2份,增稠剂0.2~0.4份。所述增稠剂包括碱溶胀增稠剂和/或聚氨酯增稠剂,优选为同时使用两种增稠剂。所述消泡剂为有机硅消泡剂。优选的,所述水性丙烯酸哑光乳液为日本昭和的CAP-4800,所述基材润湿剂为海川化工的2432、毕克化学的BYK-033中的一种或两种,所述消泡剂为巴斯夫的A10,所述成膜助剂为美国伊士曼的醇脂12,所述增稠剂为罗门哈斯的TT-935、RM-8W中的一种或两种。进一步地,所述哑光罩面清漆按如下方法制得:按所述组分配比,先将水性丙烯酸哑光乳液和去离 ...
【技术保护点】
一种哑光罩面清漆,其特征在于:包括如下质量份数的组分:水性丙烯酸哑光乳液 50~60份,去离子水 30~46份,基材润湿剂 0.05~0.1份,消泡剂 0.1~0.2份,丙二醇 1~2份,成膜助剂 1~2份,增稠剂 0.2~0.4份。
【技术特征摘要】
1.一种哑光罩面清漆,其特征在于:包括如下质量份数的组分:水性丙烯酸哑光乳液50~60份,去离子水30~46份,基材润湿剂0.05~0.1份,消泡剂0.1~0.2份,丙二醇1~2份,成膜助剂1~2份,增稠剂0.2~0.4份。2.根据权利要求1所述的哑光罩面清漆,其特征在于:所述水性丙烯酸哑光乳液为日本昭和的CAP-4800。3.根据权利要求1所述的哑光罩面清漆,其特征在于:所述基材润湿剂为海川化工的2432、毕克化学的BYK-033中的一种或两种,成膜助剂为美国伊士曼的醇脂12。4.根据权利要求1所述的哑光罩面清漆,其特征在于:所述消泡剂为有机硅消泡剂。...
【专利技术属性】
技术研发人员:仇多威,李丹,戴国军,邵帅超,李峰,李旭妍,胡效晶,
申请(专利权)人:河北晨阳工贸集团有限公司,
类型:发明
国别省市:河北,13