The invention discloses a sludge pyrolysis catalyst preparation method comprises the following steps: adding aluminum sol, aqueous solution of hydrogen peroxide pulping to modified chrysotile, adding anhydrous alcohol, salicylic acid yttrium stirring, standing, filtering, calcined residue cracking catalyst. Modified chrysotile asbestos was prepared by the following process: mixing liquid paraffin and chrysotile asbestos, adding solid paraffin, stirring to dissolve completely, adding zinc stearate, microwave treatment, filtration, washing and drying to obtain modified chrysotile. With the catalyst residue cracking the preparation method of the catalyst specific surface area greatly, the internal aperture internal connected with each other, not easy to block can effectively improve the sludge pyrolysis rate and high selectivity.
【技术实现步骤摘要】
一种油渣裂解用催化剂制备方法
本专利技术涉及油渣裂解
，尤其涉及一种油渣裂解用催化剂制备方法。
技术介绍
我国煤炭资源丰富，原煤除部分用于炼焦、转化加工外，绝大部分用于直接燃烧。将煤直接燃烧不但热效率低、对环境的破坏严重，而且煤中具有较高经济价值的富氢组分得不到合理利用。而中国石油资源短缺，原油日趋重质化、劣质化，有些原油中的重质组分残炭和金属含量均很高，导致渣油含量较高，用传统的加工方法很难高效地对其进行综合利用，目前油渣裂解用催化剂存在内部易发生堵塞、选择性差的问题，亟待解决。
技术实现思路
基于
技术介绍
存在的技术问题，本专利技术提出了一种油渣裂解用催化剂制备方法，所得催化剂比表面积极大，内部孔径相互连通，内部不易发生堵塞，可有效提高油渣裂解的速度，而且选择性高。本专利技术提出的一种油渣裂解用催化剂制备方法，包括如下步骤：向改性温石棉中加入铝溶胶、过氧化氢水溶液混合打浆，加入无水乙醇、水杨酸钇搅拌，静置，过滤，煅烧得到油渣裂解用催化剂。优选地，改性温石棉、铝溶胶、过氧化氢水溶液、无水乙醇、水杨酸钇的重量比为80-100：30-50：70-90：100-180...
【技术保护点】
一种油渣裂解用催化剂制备方法，其特征在于，包括如下步骤：向改性温石棉中加入铝溶胶、过氧化氢水溶液混合打浆，加入无水乙醇、水杨酸钇搅拌，静置，过滤，煅烧得到油渣裂解用催化剂。
【技术特征摘要】
1.一种油渣裂解用催化剂制备方法，其特征在于，包括如下步骤：向改性温石棉中加入铝溶胶、过氧化氢水溶液混合打浆，加入无水乙醇、水杨酸钇搅拌，静置，过滤，煅烧得到油渣裂解用催化剂。2.根据权利要求1所述油渣裂解用催化剂制备方法，其特征在于，改性温石棉、铝溶胶、过氧化氢水溶液、无水乙醇、水杨酸钇的重量比为80-100：30-50：70-90：100-180：4-8；过氧化氢水溶液的浓度为15-25wt％，水杨酸钇的浓度为0.01-0.02mol/L。3.根据权利要求1或2所述油渣裂解用催化剂制备方法，其特征在于，包括如下步骤：按重量份向80-100份改性温石棉中加入30-50份铝溶胶、70-90份浓度为15-25wt％过氧化氢水溶液混合打浆20-40min，加入100-180份无水乙醇、4-8份浓度为0.01-0.02mol/L水杨酸钇搅拌10-20min，搅拌速度为1000-2000r/min，静置8-...
【专利技术属性】
技术研发人员：唐来蓉，
申请(专利权)人：望江县大唐资源再生有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。