The invention discloses a methyl terminated methyl vinyl silicone rubber synthetic method, eight methyl siloxane ring four (D4), four methyl four vinyl siloxane ring four (VMC) mixed vacuum dehydration of methyl capping agent alone drying, then go into the polymerization kettle, adding alkali glue polymerization catalyst, by adjusting the mixing current frequency, to ensure the smooth process by sticking up, heat balance, breaking off medium low viscosity, to obtain methyl terminated type methyl vinyl silicone rubber. The present invention by dry processing, methyl capping agent on water content of nitrogen regulation of dehydration, polymerization viscosity rose process, ensure that the preparation of stable quality, low gel index, molecular weight distribution, good uniformity and processing performance.
【技术实现步骤摘要】
一种甲基封端型甲基乙烯基硅橡胶的合成方法
本专利技术涉及一种甲基乙烯基硅橡胶的合成方法，特别是一种甲基封端型甲基乙烯基硅橡胶的合成方法。
技术介绍
有机硅因其有独特的性能而广泛应用于国民经济所有的领域，如农业部门、电子/电器行业、纺织工业、生物医学、汽车工业以及航空航天工业。而硅橡胶更是有机硅行业中产值最大的领域，2015年，硅橡胶占国内橡胶消费总量的15％，即硅橡胶消费量达到150万吨，而到2020年，预计有望达到33％，即500万吨。换而言之，硅橡胶产业的发展潜力和远期发展都非常诱人，其高速发展也必将对上下游产业产生极为深远的影响。目前，甲基乙烯基硅橡胶已占据硅橡胶市场主体，主要产品为乙烯基封端型甲基乙烯基硅橡胶，相比于乙烯基封端型甲基乙烯基硅橡胶，甲基封端型甲基乙烯基硅橡胶市场需求量不大，但具有其不可替代的作用，被广泛用于下游产品的添加剂，用于特殊力学性能的产品，由于产品质量稳定，硅羟基含量低、分子量分布均匀，其结构化良好，耐储存，且力学性能及加工性能优良。许多客户求购高品质的甲基封端型甲基乙烯基硅橡胶用于实验室研发或中试放大应用，以便开发性能更好的硅橡胶产...
【技术保护点】
一种甲基封端型甲基乙烯基硅橡胶的合成方法，其特征在于，包括以下步骤：将八甲基环四硅氧烷（D4）、四甲基四乙烯基环四硅氧烷（VMC）进行混合真空脱水，对甲基封端剂进行单独干燥，然后一起进入聚合釜，并加入碱胶催化剂聚合，通过调节搅拌电流频率，确保涨粘过程平稳，经保温平衡后，破媒脱低出胶，即得到甲基封端型的甲基乙烯基硅橡胶。
【技术特征摘要】
1.一种甲基封端型甲基乙烯基硅橡胶的合成方法，其特征在于，包括以下步骤：将八甲基环四硅氧烷（D4）、四甲基四乙烯基环四硅氧烷（VMC）进行混合真空脱水，对甲基封端剂进行单独干燥，然后一起进入聚合釜，并加入碱胶催化剂聚合，通过调节搅拌电流频率，确保涨粘过程平稳，经保温平衡后，破媒脱低出胶，即得到甲基封端型的甲基乙烯基硅橡胶。2.根据权利要求1所述的方法，其特征在于：所述的甲基封端剂为六甲基二硅氧烷（MM）或5～500cst二甲基硅油。3.根据权利要求1所述的方法，其特征在于：甲基封端剂进行干燥时所用的干燥剂为为氢化钙、多孔分子筛、粘土干燥剂中的一种或几种。4.根据权利要求1所述的方法，其特征在于：所述八甲基环四硅氧烷与甲...