一种耐用超疏水织物及其制备方法技术

本发明专利技术公开了一种耐用超疏水织物及其制备方法。该制备方法是将织物浸入正硅酸乙酯和含端羟基的聚二甲基硅氧烷的混合溶液中，取出后置于装有盐酸溶液的密闭容器中且位于盐酸溶液液面之上，在30‐60℃温度下反应0.5‐2h，制得耐用超疏水织物。本发明专利技术制备的织物表面水滴静态接触角大于150°，水滴在其表面极易滚动，同时该织物具有优异的化学稳定性和力学耐久性，且制备工艺简单，无污染。

Durable super hydrophobic fabric and preparation method thereof

The invention discloses a durable super hydrophobic fabric and a preparation method thereof. The preparation method is immersed in the fabric of TEOS and hydroxyl terminated poly two methyl siloxane mixture, in a sealed container after removal of hydrochloric acid solution in hydrochloric acid solution and is positioned above the liquid level, 0.5 - 2H reaction at 30 - 60 Deg. C, made of durable superhydrophobic fabric. The preparation method of the fabric surface water static contact angle greater than 150 degrees, water droplets on the surface of rolling extremely easily, the chemical stability and mechanical fabric has excellent durability, and simple preparation process, no pollution.

【技术实现步骤摘要】
一种耐用超疏水织物及其制备方法
本专利技术涉及一种超疏水材料，具体涉及一种耐用超疏水织物及其制备方法。
技术介绍
受自然界中荷叶表面、蝴蝶翅膀、动物羽毛等的启发，人们设计并专利技术了超疏水织物，其静态液滴接触角大于150°，且水滴在其表面极易发生滚动。超疏水织物在自清洁、防覆冰、防污染、阻燃、油水分离等方面具有重要的应用价值，已引起了人们的广泛关注。目前关于超疏水织物的制备方法已有较多报道，如化学刻蚀法、溶胶凝胶法、气相沉积法、紫外光固化法等，但仍存在如下问题：制备工艺繁琐，反应条件苛刻，需要用到特殊的昂贵仪器，只能局限于实验室研究；采用含氟的低表面能物质修饰织物以期构造超疏水表面，但长链含氟单体容易在自然环境中氧化分解，对人体健康和生态环境会造成严重的危害；制备过程中四氢呋喃、甲苯、丙酮等有毒溶剂的使用也违背了“绿色化学”的宗旨；构造出的微纳粗糙结构由于与织物、低表面能物质间微弱的结合力容易遭到破坏，导致织物抵抗外界破坏能力差，在洗涤或摩擦后易丧失超疏水性，耐用性较差。因此，发展一种制备方法简便、经济高效、绿色环保和耐用性强的超疏水织物显得尤为重要。
技术实现思路
本专利技术针对目前超本文档来自技高网...

【技术保护点】
一种耐用超疏水织物的制备方法，其特征在于包括以下步骤：将织物浸入正硅酸乙酯和含端羟基的聚二甲基硅氧烷的混合溶液中，取出后置于装有盐酸溶液的密闭容器中且位于盐酸溶液液面之上，在30‐60℃温度下反应0.5‐2h，制得耐用超疏水织物。

【技术特征摘要】
1.一种耐用超疏水织物的制备方法，其特征在于包括以下步骤：将织物浸入正硅酸乙酯和含端羟基的聚二甲基硅氧烷的混合溶液中，取出后置于装有盐酸溶液的密闭容器中且位于盐酸溶液液面之上，在30‐60℃温度下反应0.5‐2h，制得耐用超疏水织物。2.根据权利要求1所述的耐用超疏水织物的制备方法，其特征在于：所述含端羟基的聚二甲基硅氧烷的分子量为400‐8000。3.根据权利要求1所述的耐用超疏水织物的制备方法，其特征在于：所述正硅酸乙酯和含端羟基的聚二甲基硅氧烷的质量比为2:1‐5:1。4.根据权利要求1所述的耐用超疏水织物的制备方法，其特征在于：所述盐酸溶液的质...

【专利技术属性】
技术研发人员：李红强，苏晓竞，曾幸荣，赖学军，张林，
申请(专利权)人：华南理工大学，
类型：发明
国别省市：广东,44