The invention discloses a steel surface rust inhibitor combination products and applications are divided into independent use of coating agent, detergent, soaking agent, passivating agent, mixed liquid coating is used as a potassium hydroxide and ammonium sulfate, triethanolamine; the detergent mixture of nitric acid and thiourea; soaking agent for the solution of ammonium chloride and zinc chloride solution; the mixed liquid passivating agent for chromate and dichromate. The steel surface rust inhibitor composite product can be used to treat the surface of the steel, so that the surface evenness of the steel product is high and the surface roughness is low. More importantly, the rust resistance of the steel surface is greatly enhanced. And for a long time to maintain the good appearance of the outside surface of steel.
【技术实现步骤摘要】
一种钢材表面防锈剂组合产品及其应用
本专利技术属于精细化学品生产
领域，涉及一种防锈剂，具体涉及一种钢材表面防锈剂组合产品及其应用。
技术介绍
钢材是国家建设和实现四化必不可少的重要物资，其应用广泛、品种繁多，根据断面形状的不同、钢材一般分为型材、板材、管材和金属制品四大类，为了便于组织钢材的生产、订货供应和搞好经营管理工作，又分为重轨、轻轨、大型型钢、中型型钢、小型型钢、钢材冷弯型钢，优质型钢、线材、中厚钢板、薄钢板、电工用硅钢片、带钢、无缝钢管钢材、焊接钢管、金属制品等品种。钢材应用广泛、品种繁多，根据断面形状的不同，钢材一般分为型材、板材、管材和金属制品四大类。钢材是钢锭、钢坯或钢材通过压力加工制成的一定形状、尺寸和性能的材料。大部分钢材加工都是通过压力加工，使被加工的钢(坯、锭等)产生塑性变形。根据钢材加工温度不同，可以分为冷加工和热加工两种。钢铁的锈蚀实际上是一种氧化反应，当钢铁氧化后，钢表面就形成的红褐色的氧化铁。然而不幸的是：普通钢表面在形成的氧化铁后，锈蚀并没停止，依然会继续氧化，使锈蚀不断扩大，最终造成物件的毁损。而在海水或潮湿，高热环境气...
【技术保护点】
一种钢材表面防锈剂组合产品，其特征在于所述的防锈剂组合产品分为各自独立使用的涂覆剂、洗涤剂、浸泡剂、钝化剂，所述的涂覆剂为氢氧化钾与硫化铵、三乙醇胺的混合液；所述的洗涤剂为硝酸与硫脲的混合液；所述的浸泡剂为氯化铵溶液及氯化锌溶液；所述的钝化剂为重铬酸铵与铬酸的混合液。
【技术特征摘要】
1.一种钢材表面防锈剂组合产品，其特征在于所述的防锈剂组合产品分为各自独立使用的涂覆剂、洗涤剂、浸泡剂、钝化剂，所述的涂覆剂为氢氧化钾与硫化铵、三乙醇胺的混合液；所述的洗涤剂为硝酸与硫脲的混合液；所述的浸泡剂为氯化铵溶液及氯化锌溶液；所述的钝化剂为重铬酸铵与铬酸的混合液。2.根据权利要求1所述的钢材表面防锈剂组合产品，其特征在于所述的涂覆剂为2～5％的氢氧化钾与13～16％的硫化铵、1～2％的三乙醇胺的混合液。3.根据权利要求1所述的钢材表面防锈剂组合产品，其特征在于所述的洗涤剂为10～12％的硝酸与0.1～0.2％硫脲的混合液。4.根据权利要求1所述的钢材表面防锈剂组合产品，其特征在于所述的浸泡剂为浓度为100～150g/L的氯化铵溶液；及浓度为150～180g/L的氯化锌溶液。5.根据权利要求1所述的钢材表面防锈剂组合产品，其特征在于所述的钝化剂为浓度为80～100g/L的重铬酸铵溶液与浓度为3～4g...