The embodiment of the invention discloses a rare earth salt passivation liquid and a preparation method thereof, relating to the technical field of metal surface material treatment. The rare earth salt passivation solution is prepared from the following raw materials: rare earth salt, sodium silicate, organic silane, metal complexing agent, phosphoric acid, acid complexing agent, ethylene glycol, ethylene diamine EDTA, two sodium, water. The rare earth salt is added to improve the corrosion resistance of the passivation layer, so that the corrosion current density is decreased, the polarization resistance is raised, and the utility model has the advantages of cleanness, environmental protection and no toxic substances, and is stable and reliable.
【技术实现步骤摘要】
一种稀土盐钝化液及其制备方法
本专利技术涉及金属表面材料处理
，尤其涉及一种稀土盐钝化液及其制备方法。
技术介绍
钝化使镀层的耐腐蚀性能进一步的提高并增加表面光泽和抗污染的能力。如经过化学镀、电镀、酸洗、水洗等处理的工件表面非常活泼，所以要立即进行钝化处理，使处理后的金属表面形成一层保护膜，减缓腐蚀。对工件进行全面的钝化处理，可以提高其抗腐蚀性能，延长使用寿命。金属表面进行钝化处理通常使用的是铬酸盐钝化。铬酸盐钝化膜致密，本身又耐蚀，与基体金属的结合力牢固，并且能够对裸漏处的金属表面再次钝化，对进一步腐蚀起到了抑制作用，即通常所说的“自愈能力”。然而，六价铬化合物有很高的毒性，是致癌物质。随着人们环境保护意识的增强，对于有毒有害物的控制日益强化。为此，许多替代六价铬的对策和工艺已经被广泛的提出来了。稀土盐与有机硅烷处理的复合膜成为目前钝化工艺发展方向，越来越多的研究指出稀土盐钝化膜其耐腐蚀性接近，达到，超多六价铬钝化膜的性能。
技术实现思路
本专利技术的实施例提供一种稀土盐钝化液及其制备方法，钝化耐蚀性强，并且清洁环保，不含毒性物质，稳定可靠。为达到上述目的，本...
【技术保护点】
一种稀土盐钝化液，其特征在于，包括以下的原料制备而成：稀土盐，硅酸钠，有机硅烷，金属络合剂，磷酸，酸类络合剂，乙二醇，乙二胺四乙酸二钠，水。
【技术特征摘要】
1.一种稀土盐钝化液，其特征在于，包括以下的原料制备而成：稀土盐，硅酸钠，有机硅烷，金属络合剂，磷酸，酸类络合剂，乙二醇，乙二胺四乙酸二钠，水。2.根据权利要求1所述的一种稀土盐钝化液，其特征在于，包括以下份数的原料制备而成：稀土盐15-30g/L,硅酸钠5-15g/L，有机硅烷0.5-15g/L，金属络合剂3-8g/L，磷酸10-30mL/L，酸类络合剂5-10g/L，乙二醇10-20g/L，乙二胺四乙酸二钠5-15g/L，其余为水。3.根据权利要求1所述的一种稀土盐钝化液，其特征在于，所述稀土盐是硝酸亚铈，氯化亚铈，硫酸亚铈的一种或多种混合物。4.根据权利要求1所述的一种稀土盐钝化液，其特征在于，所述有机硅烷是羟基乙叉二磷酸、3-氨丙基三已氯基硅烷、硫酸羟胺、γ-缩水甘油醚氧丙基三甲氧基硅烷中的一种。5.根据权利要求1所述的一种稀土盐钝化液，其特征在于，所述金属络合剂...
【专利技术属性】
技术研发人员：刘刚，王梅凤，汤成平，高进，唐敏，薛云峰，
申请(专利权)人：句容市博远电子有限公司，
类型：发明
国别省市：江苏,32