The invention relates to a stainless steel pickling passivation liquid, which uses nitric acid (HNO3) and hydrofluoric acid (HF) as the main raw material, and then adds a proper amount of water to make the liquid mixed. The passivation of stainless steel, stainless steel surface can effectively remove the rust and grease, welding spots and dirt, make the stainless steel get uniform silver surface and form a layer of thin and compact passivation film, has a very good role on the corrosion resistance of stainless steel, is widely applied. The volume content of stainless steel pickling passivation liquid of the invention is nitric acid (HNO3) 15%, hydrofluoric acid (HF) 10% and water (H2O) 75%.
【技术实现步骤摘要】
本专利技术涉及一种不锈钢酸洗钝化液,尤其是用硝酸(HNO3)、氢氟酸(HF)和水(H2O),根据不同的比例进行的制备。
技术介绍
酸洗钝化,就是一种化学反应,用以除去不锈钢表面的腐锈、油污等污垢,同时形成均匀致密的钝化膜,提高不锈钢的防腐蚀性能。一种不锈钢酸洗钝化液,是以硝酸(HNO3)、氢氟酸(HF)为主要原料,再加入适量水中经混合后制得的溶液。这种不锈钢酸洗钝化液,能够有效清除不锈钢表面的腐锈、油污、焊斑等污垢,并形成一层均匀致密的钝化膜,大大提高不锈钢的防腐蚀性能,在不锈钢零件、板材、设备中得到较为广泛的应用。
技术实现思路
本专利技术的目的在于提供一种具有提高不锈钢防腐性能的酸洗钝化液。本专利技术通过如下方式实现目的:本专利技术不锈钢酸洗钝化液含有硝酸(HNO3)15L、氢氟酸(HF)10L、水(H2O)75L。所述的硝酸(HNO3)为具有强氧化性和腐蚀性的强酸,浓度约为95%,有很强的氧化腐蚀作用;氢氟酸(HF)是一种弱酸,但对金属具有极强的腐蚀能力;经混合后制得的酸洗钝化液,能够很好地去除不锈钢表面的各种污垢,并形成均匀致密的钝化膜,提高不锈钢的耐腐蚀性能。本专利技术的制备方法:将硝酸(HNO3)、氢氟酸(HF)和水(H2O)等按相应比例进行混合,混合均匀后,即可得到所需的不锈钢酸洗钝化液。本方法使用了硝酸(HNO3),有很强的酸性,对不锈钢表面有一定的氧化腐蚀作用。而氢氟酸(HF)是一种弱酸,但对不锈钢表面有极强的腐蚀作用。两种物质按一定比例加水混合后形成的酸洗钝化液,可对不锈钢表面起到去污、形成钝化膜、提高防腐性能的作用。具体实施方式以下结合 ...
【技术保护点】
一种不锈钢酸洗钝化液,其特征在于由如下物质组成:硝酸(HNO3) 15L氢氟酸(HF) 10L水(H2O) 75L。
【技术特征摘要】
1.一种不锈钢酸洗钝化液,其特征在于由如下物质组成:硝酸(HNO3)15L氢氟酸(HF)10L水(H2O)75L。2.根据权利要求1所述的一种不锈钢酸洗钝化液,其特征在于:使用了...