The embodiment of the invention discloses an environmental protection type phosphating solution and a preparation method thereof, relating to the technical field of metal surface material treatment. The environmental protection type phosphating solution by weight of a raw material for the following: 80 prepared 85% phosphoric acid 30 phosphate 20 50 copies, 50 copies, 50 copies of molybdate 20, citric acid 10 20, 5 surfactant 10, octylphenol polyoxyethylene ether 5 10, dispersion agent 10 20. The invention does not use harmful substances such as nitrate, nitrite, chromate, etc. the utility model has the advantages of green environment protection and strong rust resistance, and the corrosion resistance of the phosphating film formed by the phosphating film is good.
【技术实现步骤摘要】
一种环保型磷化液及其制备方法
本专利技术涉及金属表面材料处理
，尤其涉及一种环保型磷化液及其制备方法。
技术介绍
磷化是指金属零件在磷酸盐溶液中发生化学反应、电化学反应等，在金属表面形成一层难溶的磷化膜的过程。金属在磷化处理后可提高金属涂膜的附着力，耐腐蚀性及其防护性能。但是，现在用的磷化处理剂一般具有强腐蚀性，在使用和储存过程中，难以摆脱化学除锈带来的危害，如产生有毒的刺激性气味等。随着人们对环保要求的提高，专利技术一种无污染，无危害的磷化液成为一个迫切解决的问题。目前国内磷化技术普遍存在的问题是：磷化温度高、磷化液使用寿命短、水洗难度大以及造成水体污染等问题，不仅给环境治理带来负担而且消耗大量的水、磷酸盐等资源。因此磷化技术的发展方向，主要是提高质量和降低污染、节能、无毒环保，进一步是清洁磷化，磷化液应该具有节约材料与能源、功能合理，产品在使用过程中及使用后不危害人体健康和破坏生态环境的特点。
技术实现思路
本专利技术的实施例提供一种环保型磷化液及其制备方法，绿色环保，同时防锈能力强，其形成的磷化膜抗腐蚀性能良好。为达到上述目的，本专利技术的实施例采用如下技...
【技术保护点】
一种环保型磷化液，其特征在于，包括以下的重量份数的原料制备而成：80‑85%磷酸30‑50份，磷酸盐20‑50份，钼酸盐20‑50份，柠檬酸10‑20份，表面活性剂5‑10份，辛基苯酚聚氧乙烯醚5‑10份，分散剂10‑20份。
【技术特征摘要】
1.一种环保型磷化液，其特征在于，包括以下的重量份数的原料制备而成：80-85%磷酸30-50份，磷酸盐20-50份，钼酸盐20-50份，柠檬酸10-20份，表面活性剂5-10份，辛基苯酚聚氧乙烯醚5-10份，分散剂10-20份。2.根据权利要求1所述的环保型磷化液，其特征在于，包括以下重量份数的原料制备而成：80-85%磷酸35-45份，磷酸盐30-40份，钼酸盐30-40份，柠檬酸10-15份，表面活性剂5-8份，辛基苯酚聚氧乙烯醚5-8份，分散剂10-15份。3.根据权利要求1所述的环保型磷化液，其特征在于，所述磷酸盐是磷酸锌、磷酸二氢锌、磷酸锰、磷酸二氢锰、磷酸钙或磷酸二氢钙中的一种或多种混合物。4.根据权利要求1所...
【专利技术属性】
技术研发人员：刘刚，王梅凤，汤成平，高进，唐敏，薛云峰，
申请(专利权)人：句容市博远电子有限公司，
类型：发明
国别省市：江苏,32