一种镀膜玻璃及其制备方法技术

本发明专利技术公开了一种镀膜玻璃，包括玻璃基板和设于玻璃基板一面的膜层，所述膜层自玻璃基板向外依次分布为：第一复合层、第一功能层、第二复合层、第二功能层、保护层、变色层、抗污层，本发明专利技术还公开了该镀膜玻璃的制备方法，主要采用真空磁控溅射方法制备。通过本发明专利技术的制备方法制备的该镀膜玻璃，具有防污，抗氧化，变色及隔热等多重功能。

Coated glass and preparation method thereof

The invention discloses a film coated glass, including glass substrate and glass substrate is arranged on the side of the film from the glass substrate outside distribution: first the first composite layer, function layer, second layer, second layer composite function, protective layer, color layer, anti fouling layer, the invention also discloses a method for preparing the preparation of the coated glass, mainly by vacuum magnetron sputtering. The coated glass prepared by the method of preparation of the present invention has many functions such as antifouling, oxidation resistance, discoloration and heat insulation.

【技术实现步骤摘要】
一种镀膜玻璃及其制备方法
本专利技术涉及玻璃制造
，尤其涉及一种镀膜玻璃及其制备方法。
技术介绍
玻璃是重要的建筑材料，随着对建筑物装饰性要求的不断提高，玻璃在建筑行业中的使用量也不断增大。然而，当今人们在选择建筑物的玻璃门窗时，除了考虑其美学和外观特征外，更注重其热量控制、制冷成本和内部阳光投射舒适平衡等问题。这就使得镀膜玻璃家族中的新贵——Low-E玻璃脱颖而出，成为人们关注的焦点。Low-E玻璃又称低辐射玻璃，是在玻璃表面镀上多层金属或其他化合物组成的膜系产品。其镀膜层具有对可见光高透过及对中远红外线高反射的特性，使其与普通玻璃及传统的建筑用镀膜玻璃相比，具有以下明显优势：优异的热性能外门窗玻璃的热损失是建筑物能耗的主要部分，占建筑物能耗的50%以上。有关研究资料表明，玻璃内表面的传热以辐射为主，占58%，这意味着要从改变玻璃的性能来减少热能的损失，最有效的方法是抑制其内表面的辐射。普通浮法玻璃的辐射率高达0.84，当镀上一层以银为基础的低辐射薄膜后，其辐射率可降至0.1以下。因此，用Low-E玻璃制造建筑物门窗，可大大降低因辐射而造成的室内热能向室外的传递，达到理想的节本文档来自技高网...

【技术保护点】
一种镀膜玻璃，包括玻璃基板和设于玻璃基板一面的膜层，其特征在于：所述膜层自玻璃基板向外依次分布为：第一复合层、第一功能层、第二复合层、第二功能层、保护层、变色层、抗污层。

【技术特征摘要】
1.一种镀膜玻璃，包括玻璃基板和设于玻璃基板一面的膜层，其特征在于：所述膜层自玻璃基板向外依次分布为：第一复合层、第一功能层、第二复合层、第二功能层、保护层、变色层、抗污层。2.根据权利要求1所述的镀膜玻璃，其特征在于：所述第一复合层与第二复合层由ZnO和TiO2混合组成，所述第一复合层与第二复合层的厚度为50~150nm。3.根据权利要求2所述的镀膜玻璃，其特征在于：所述ZnO的重量百分比为20%-80%，所述TiO2的重量百分比为80%-20%。4.根据权利要求1所述的镀膜玻璃，其特征在于：所述第一功能层和第二功能层为Ag层，第一功能层和第二功能层的厚度为20~30nm。5.根据权利要求1所述的镀膜玻璃，其特征在于：所述保护层为铑层，该铑层的厚度为15~25nm。6.根据权利要求1所述的镀膜玻璃，其特征在于：所述变色层为卤化银，该变色层的厚度为0.01-0.1nm。7.根据权利要求1所述的镀膜玻璃，其特征在于：所述抗污层为氟化有机硅烷聚合物，该抗污层的厚度为0.005~...

【专利技术属性】
技术研发人员：彭傲寒，吴志勇，刘源，饶建超，
申请(专利权)人：湖北弘港科技有限公司，
类型：发明
国别省市：湖北,42