The invention discloses a Aluminum Alloy, among them, the total weight of the Aluminum Alloy for reference, including the composition of the Aluminum Alloy: aluminum content is 82.9-97.99%, the nickel content is 2-8%, the zinc content is greater than 0 wt% and 6 wt%, the content of silicon more than 0 wt% and 2 wt%, the iron content of 0.01-0.1 wt%, the magnesium content is greater than 0 wt% and 1 wt% or less. The invention also provides a preparation method of the aluminum alloy. According to the aluminum alloy and the preparation method thereof, an aluminum alloy with a coefficient of thermal conductivity of 170W/ (m, K) and a yield strength above 100Mpa and an elongation of more than 2 can be obtained.
【技术实现步骤摘要】
一种铝合金及其制备方法
本专利技术涉及铝合金及其制备方法，具体地，涉及一种高导热铸造铝合金及其制备方法。
技术介绍
铝合金加工性能好，尤其是亚共晶铝硅合金，其不仅加工性能好，而且比重轻，表面美观且耐腐蚀，铸造性能好，制品综合力学性能好，热处理后强度可以大幅度提高，是优良的铸造合金，可用于各种各样的形状复杂的部件，在许多领域中得到广泛应用。电子产品由于通常需要复杂精密的结构件，因此压铸合金成为常用的结构件。随着电子产品变的越来越薄、越来越轻、功能越来越多，对散热要求也越来越高，因此，高热导率铸造铝合金具有重要的应用前景。然而目前最常用的压铸铝合金是ADC12(Aluminum-AlloyDieCastings12)，该合金具有良好的铸造性能、机械强度及耐蚀性能，因此得到广泛应用。但该合金的热导率较低，只有92W/(m·K)，不能满足现有电子产品散热要求。因此迫切需要开发一种既具有优良的机械性能又具有高导热系数同时具有良好耐腐蚀性的铸造铝合金，以满足电子产品发展的需求。
技术实现思路
本专利技术的目的在于克服现有的铸造铝合金的导热系数较低的缺陷，提供一种具有良好的机械性能...
【技术保护点】
一种铝合金，其特征在于，以该铝合金的总重量为基准，所述铝合金的组成包括：铝的含量为82.9‑97.99重量％，镍的含量为2‑8重量％，锌的含量为大于0重量％且为6重量％以下，硅的含量为大于0重量％且为2重量％以下，铁的含量为0.01‑0.1重量％，镁的含量大于0重量％且为1重量％以下。
【技术特征摘要】
1.一种铝合金，其特征在于，以该铝合金的总重量为基准，所述铝合金的组成包括：铝的含量为82.9-97.99重量％，镍的含量为2-8重量％，锌的含量为大于0重量％且为6重量％以下，硅的含量为大于0重量％且为2重量％以下，铁的含量为0.01-0.1重量％，镁的含量大于0重量％且为1重量％以下。2.根据权利要求1所述的铝合金，其特征在于，以该铝合金的总重量为基准，所述铝合金的组成包括：铝的含量为90.15-96.38重量％，镍的含量为2.5-5重量％，锌的含量为1-3重量％，硅的含量为0.5-1.5重量％，铁的含量为0.02-0.05重量％，镁的含量0.1-0.5重量％。3.根据权利要求1或2所述的铝合金，其特征在于，所述铝合金还包括不可避免的杂质元素：铜≤0.01重量％，钴≤0.01重量。4.根据权利要求1或2所述的铝合金，其特征在于，所述铝合金的导热系数为170W/(m·K)以上，屈服强度为100Mpa以上，延伸率为2以上。5.根据权利要求4所述的铝合金，其特征在于，所述铝合金的导热系数为175-190W/(m·K)，屈服强度为105-125Mpa，延伸率为2.5-5。6.一种铝合金的制...
【专利技术属性】
技术研发人员：文丹华，吴波，
申请(专利权)人：比亚迪股份有限公司，
类型：发明
国别省市：广东,44