The invention relates to a control flange deformation of the inlet and outlet pipe assembly processing method, and is characterized in comprising the following steps: (1) the flange and pipe for the amount of turning welding, horizontal tooling, welding current is 115 150A, voltage is 20 23V, weld width is 3mm; (2) use the processing of CNC machine tool edge flange, the flange size and design of the same size. The flange blank is V type flange. The step (1) in the welding of stem elongation of 10 15mm, welding speed is 60 80cm/min, gas flow rate of 10 15L/min. The control of inlet and outlet pipe module processing method to reduce the deformation of the flange, welding shaping process, reduce costs, reduce labor intensity, reduce production cost, increase between the flange joint degree, increase the stability of the structure, size and high stability, meet the requirements of the customer installation.
【技术实现步骤摘要】
控制法兰变形的进出气管组件加工方法
本专利技术涉及一种汽车后处理行业中控制法兰变形的进出气管组件加工方法，属于汽车尾气后处理
技术介绍
净化消声器产品通常用法兰与发动机相连，法兰一般与管子或者端盖焊接，法兰焊接不可避免的产生焊接变形，有些法兰面带有台阶，焊后法兰发生翘曲，装车的时候和抱箍拧不紧，造成漏气，使未经过净化的废气直接排放到空气中，造成空气污染。法兰表面不平整会造成强度的明显下降，严重会造成连接部位发生断裂，造成严重的质量事故。为了提高质量和生产效率，保证产品尺寸，必须对现有的进出气管组件加工方法进行改进，达到客户的安装要求。目前在汽车尾气后处理
，通常有以下方法来控制法兰变形：（1）采用焊后对法兰整形的加工方法来保证平面度，焊后整形适合平面法兰与管子焊接的组件，对于结构复杂的组件不适合；（2）对法兰设置预变形量，这种方法可以有效减少焊接变形，但是对于带有台阶高度的V型法兰并不适用，V型法兰焊接涉及台阶高度、角度、边缘厚度等尺寸，结构比较复杂，不能完全掌握变形规律，不具有加工的稳定性。这些加工方法费时费力，增加劳动强度，规律不易掌控。专利技...
【技术保护点】
一种控制法兰变形的进出气管组件加工方法，其特征是，包括以下步骤：（1）将预留车削量的法兰毛坯（1）与管子（2）焊接，使用卧式工装，焊接电流为115‑150A，电压为20‑23V，熔宽为3mm；（2）用数控机床加工法兰边缘，使法兰尺寸和设计尺寸一致。
【技术特征摘要】
1.一种控制法兰变形的进出气管组件加工方法，其特征是，包括以下步骤：（1）将预留车削量的法兰毛坯（1）与管子（2）焊接，使用卧式工装，焊接电流为115-150A，电压为20-23V，熔宽为3mm；（2）用数控机床加工法兰边缘，使法兰尺寸和设计尺寸一致。2.如权利要...