The invention discloses a preparation method of fluorine content and size adjustable fluorinated carbon fiber, which comprises the following steps: (1) surface treatment: fluorinated carbon fiber materials will be added to the fluorinated carbon fiber surface treatment reagent, heating 60 to 150 DEG C under the protection of gas, obtained fluorinated carbon fiber pretreatment carbon fiber; (2) different sizes: fluoride separation steps (1) fluorinated carbon fiber pretreatment, after cooling by filtration, separation and washing after drying to obtain fluorinated carbon fiber. The fluorinated carbon fiber prepared by the method has the advantages of controllable fluorine content and controllable size, and the dispersion and stability are improved in the water and the organic solvent.
【技术实现步骤摘要】
本专利技术涉及一种氟化碳纤维尺寸调控及表面处理技术，尤其涉及一种制备氟含量与尺寸可调氟化碳纤维的方法。
技术介绍
碳纤维具有比强度/比模量高、抗蠕变、导电、传热和热膨胀系数小等一系列优异性能，而且耐高温、耐腐蚀、耐疲劳。因此它既能作为结构材料，又能作为功能材料使用，被广泛用于在航天、航空等高科技领域中。氟化碳纤维不但继承了碳纤维的优异性能，又因氟原子的引入带来了表面能降低、疏水性/热稳定性增强、带隙展宽及介电性能提高等新颖的界面和物理化学性能，因此氟化碳纤维除了在传统的化工、材料、机械制造领域具有重要的应用外，在新兴的表/界面科学、新型纳米电子器件、生物材料以及能源材料等领域也展示出广泛的应用前景（参见：N.Yu,H.Yin,W.Zhang,etal.Adv.EnergyMater.,2016,6,1501458;M.Srinivas1,A.Heerschap,E.T.Ahrens,etal.,TrendsBiotechno.,2010,28,363.）。氟化碳纤维可单独使用，但绝大多数是以复合材料的形式使用，因此需要经过表面处理来改善自身与其他材料复合的效果。...
【技术保护点】
一种制备氟含量与尺寸可调氟化碳纤维的方法，其特征在于，包括以下处理步骤：（1）氟化碳纤维表面处理：将原料氟化碳纤维加入到表面处理试剂中，在气体保护下加热60～150℃反应，得到预处理的氟化碳纤维；（2）不同尺寸氟化碳纤维分离：将步骤（1）中预处理的氟化碳纤维，冷却后通过滤膜抽滤，分离洗涤后经过干燥得到成品氟化碳纤维。
【技术特征摘要】
1.一种制备氟含量与尺寸可调氟化碳纤维的方法，其特征在于，包括以下处理步骤：（1）氟化碳纤维表面处理：将原料氟化碳纤维加入到表面处理试剂中，在气体保护下加热60～150℃反应，得到预处理的氟化碳纤维；（2）不同尺寸氟化碳纤维分离：将步骤（1）中预处理的氟化碳纤维，冷却后通过滤膜抽滤，分离洗涤后经过干燥得到成品氟化碳纤维。2.根据权利要求1所述的方法，其特征在于，所述步骤（1）中，原料氟化碳纤维的氟含量为0.1～65at.%。3.根据权利要求1所述的方法，其特征在于，所述步骤（1）中，所述的表面处理试剂为二胺试剂。4.根据权利要求3所述的方法，其特征在于，所述的表面处理试剂...
【专利技术属性】
技术研发人员：公培伟，孙璐，逄铭慧，张雨荷，刘哲，
申请(专利权)人：曲阜师范大学，
类型：发明
国别省市：山东;37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。