一种粒化高炉矿渣微粉改性剂制造技术

本发明专利技术公开了一种粒化高炉矿渣微粉改性剂是由下述重量配比的原料经粉碎、混合配制而成：无水硫酸钠２０～５５份，工业碳酸钠５～３０份，氯化钙１０～５０份，氯化钠１０～５０份，硫酸铝１０～３０份，粉煤灰５～１５份。本发明专利技术粒化高炉矿渣微粉改性剂，实验证明：在粒化高炉矿渣微粉中添加１％，就可以有效改善粒化高炉矿渣微粉的活性，提高粒化高炉矿渣微粉的强度等级，也可用于高细粉煤灰的制备过程，提高粉煤灰的活性，还可用于利用粒化高炉矿渣微粉或高细粉煤灰制备水泥或商品混凝土的过程，可大幅度提高粒化高炉矿渣微粉或高细粉煤灰在水泥或混凝土中的掺加量，降低水泥或混凝土的使用成本。

Granulated blast furnace slag micropowder modifier

The invention discloses a blast furnace slag powder modifier is by the weight ratio of the raw materials are crushed, mixed and compounded: anhydrous sodium sulfate from 20 to 55, 5 to 30 portions of sodium carbonate, calcium chloride and sodium chloride in 10 ~ 50, 10 ~ 50, 10 ~ 30 aluminum sulfate a fly ash 5 to 15. The invention of granulated blast furnace slag powder modifier, experiments show that after adding 1% blast furnace slag powder, can effectively improve the GGBS activity, improve the strength grade of blast furnace slag powder, also can be used in the preparation process of fine fly ash, improve the activity of fly ash and it can also be used to produce cement or concrete with blast furnace slag powder or fine fly ash, granulated blast furnace slag powder or fine fly ash in cement or concrete mixing capacity can be greatly improved, reducing the use cost of cement or concrete.

【技术实现步骤摘要】

本专利技术属于粒化高炉矿渣微粉添加剂
，涉及一种粒化高炉矿渣微粉改性剂。
技术介绍
目前，生产的粒化高炉矿渣微粉，普遍存在强度等级较低技术缺陷，将其用于制备水泥或商品混凝土，可以降低生产成本，但是，粒化高炉矿渣微粉的添加量过高，将影响其产品的质量。
技术实现思路
本专利技术的目的是提供一种粒化高炉矿渣微粉改性剂，以解决现有技术粒化高炉矿渣微粉强度等级较低等技术问题，进一步改善粒化高炉矿渣微粉的性能。本专利技术粒化高炉矿渣微粉改性剂是由下述重量配比的原料经粉碎、混合配制而成无水硫酸钠20～55份，工业碳酸钠5～30份，氯化钙10～50份，氯化钠10～50份，硫酸铝10～30份，粉煤灰5～15份。本专利技术粒化高炉矿渣微粉改性剂，实验证明在粒化高炉矿渣微粉中添加1％，就可以有效改善粒化高炉矿渣微粉的活性，提高粒化高炉矿渣微粉的强度等级，也可用于高细粉煤灰的制备过程，提高粉煤灰的活性，还可用于利用粒化高炉矿渣微粉或高细粉煤灰制备水泥或商品混凝土的过程，可大幅度提高粒化高炉矿渣微粉或高细粉煤灰在水泥或混凝土中的掺加量，降低水泥或混凝土的制造成本。附图说明附图是本专利技术工艺流程图 具本文档来自技高网...

【技术保护点】
一种粒化高炉矿渣微粉改性剂，其特征是由下述重量配比的原料经粉碎、混合配制而成：无水硫酸钠２０～５５份，工业碳酸钠５～３０份，氯化钙１０～５０份，氯化钠１０～５０份，硫酸铝１０～３０份，粉煤灰５～１５份。

【技术特征摘要】

【专利技术属性】
技术研发人员：李跃宏，
申请(专利权)人：李跃宏，
类型：发明
国别省市：37[中国|山东]