A kind of steel slag sand mortar, mainly composed of cement, sand or adding a small amount of additive mixture, which partially or completely replace steel slag sand sand, slag sand sand rate is = 20% - 100%, modifier and adding a certain amount of. Specifically, the steel slag sand dry powder mortar of the invention, according to the mass ratio of the composition is: cement: Sand: sand, slag modifier = 1: 0: 3.5: 0.5: 5: 0.05 - 0.2. Its production process is as follows: (1) raw material testing and drying; (2) preparing modifier; (3) the cement, sand, sand and / or slag modifier according to the proportion of mixed system of steel slag sand dry mortar products; (4) consistency, stratification and stability test (5; metering, packaging and warehousing) or bulk storage. The invention is of great importance to the utilization of the waste resources, the energy conservation and the environment protection, and the performance of the mortar is improved.
【技术实现步骤摘要】
本专利技术涉及废弃资源的综合利用，尤指钢铁工业生产过程中产生的钢渣的利用，具体指一种以钢渣砂部分或全部替代黄砂的钢渣砂干粉砂浆。
技术介绍
钢渣是钢厂生产过程中产生的主要废渣之一，其排放量约占钢产量的15-20％，数量非常巨大，是钢厂综合利用的重中之重。由于钢渣成分波动大、安定性差、磨碎困难等原因，其综合处理及开发利用存在一定的难度。钢渣有转炉浅盘水淬钢渣，转炉滚筒钢渣，电炉钢渣等多种类型，单上海宝钢的年排放量就在百万吨以上，对钢渣的开发研究，无论在资源的充分利用方面，还是在节约能源及保护环境等方面都有着重要的经济意义和社会意义。建筑砂浆是建筑工程中用量非常大的建筑材料。传统的建筑砂浆(砌筑砂浆、抹灰砂浆和地面砂浆)主要有水泥砂浆和水泥石灰混合砂浆二大类，由于在现场配制往往质量不太稳定、强度达不到要求，容易出现开裂、空鼓和脱落等问题，而且施工现场环境差。商品干粉砂浆是近年来大量推广且发展迅速的建筑砂浆应用新技术，它较好地解决了传统砂浆存在的上述缺陷。目前比较常用的普通干粉砂浆是一种由专业厂生产的，主要由水泥、黄砂或加入少量外掺剂混合而成的一种水泥干粉砂浆，该砂...
【技术保护点】
一种钢渣砂干粉砂浆，主要由水泥、黄砂或加入少量外掺剂混合而成，其特征在于以钢渣砂部分或全部替代黄砂，钢渣砂的代砂率为≥２０％－１００％，并加入一定量的改性剂，其组成按质量比为，水泥∶黄砂∶钢渣砂∶改性剂＝１∶０－３．５∶０．５－５∶０．０５－０．２。
【技术特征摘要】
【专利技术属性】
技术研发人员：顾文飞，陈元峻，徐莉，唐欧靖，
申请(专利权)人：上海宝钢综合开发公司，
类型：发明
国别省市：31[中国|上海]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。