The invention relates to a method for improving the T bending resistance of color steel plate based on carrier control technology. This method is a mineral salt Na2CO3, Na2SO4 or BaSO4 in the ground into powder, and then prepared into suspension, while the pH value is adjusted to 7.5 to 8.5, standing, filtering and drying; the nanometer powder three EPDM coating, nano powder and three EPDM rubber the mass ratio of 1: 2 to 6.5; the quality of nano powder and coil coating ratio of 1: 4 to 8 were mixed and milled for 38 to 48 hours. With the increase of carrier concentration and order of magnitude in the coating, the bending value of T film also increases. Moreover, when the carrier concentration increases by about 2 orders of magnitude, the T value of the coating will rise by 3 - 4T accordingly.
【技术实现步骤摘要】
本专利技术涉及表面处理
，是基于载流子控制技术来提高彩钢板表面涂层 耐T弯时效。
技术介绍
彩色涂层钢板(彩钢板)是重要的钢铁厂冷轧产品之一。彩钢板生产技术首创于 1927年的美国，1959年建成世界第一套带钢连续彩涂生产机组，随后20世纪60年代， 彩涂板生产技术迅速发展，现全世界年生产能力在1400万吨左右。我国彩涂板生产技术 起步较晚，80年代末期才陆续建设彩涂机组。至今我国建成彩钢板生产线200余条。若 以每条生产线年产10万吨计，将形成十分可观的产能。但是，随着我国国民经济的调整 和发展，彩钢板的T弯时效问题逐渐成为彩钢板生产的首要问题之一，每年因彩钢板T弯 时效问题造成的高档彩钢板判废或降级率为6% -10%。 彩钢板的T弯即采用折板机沿彩钢板试样50mm处弯折180度，采用专用胶带在 试样弯折处均匀用力压着，将胶带撕开，胶带上若无漆膜附着，则记为OT。胶带上若有 漆膜附着，则继续弯折，直到经过n次弯折，在弯折处撕开胶带上无漆膜附着，则记为 (n-l)T。对于彩钢板用户来说，要求T弯值越小越好，这样可以保证彩钢板出厂的后续深 冲、折弯加工性能良...
【技术保护点】
一种基于载流子控制技术提高彩钢板耐Ｔ弯时效的方法，是通过在卷钢涂料中加入纳米活性粉体来进行改性，其特征在于该方法的具体操作步骤如下： １）采用高速球磨机将成份为Ｎａ↓［２］ＣＯ↓［３］、Ｎａ↓［２］ＳＯ↓［４］或ＢａＳＯ↓［４］中的一种矿物盐研磨成纳米粉体，粒径保持在１０～１００ｎｍ范围内，然后将纳米粉体配制成１０～２５％（ｗｔ％）的悬浮液，同时调节ｐＨ值为７．５～８．５，静置３～６小时后进行抽滤，接着将所得滤饼在２００～４５０℃下烘干，直到滤饼变为干燥的白色细晶态物质，即得纳米粉体； ２）对步骤１所得的纳米粉体进行包覆处理，以三元乙丙橡胶作为包覆剂，其中纳米粉...
【技术特征摘要】
【专利技术属性】
技术研发人员：钟庆东，林海，盛敏奇，王懿，陈大洋，周琼宇，
申请(专利权)人：上海大学，
类型：发明
国别省市：31[]