The application provides a preparation method of ZSM \u2011 5 molecular sieve, which comprises the following steps: a) mixing a part of water from aluminum source, alkali source and total water consumption, and then adding template agent for mixing; b) adding silicon source and stirring crystallization at 100 \u2103 ~ 120 \u2103; c) adding remaining water and continuing crystallization at 150 \u2103 ~ 180 \u2103 to obtain ZSM \u2011 5 molecular sieve. In the invention, granular silica gel, cheap template and a small amount of water are used to prepare nano ZSM \u2011 5 molecular sieve with good crystal form, high crystallinity and high yield by adjusting template concentration and changing crystallization temperature in the crystallization process by adding water in sections. The method has low cost of raw materials, short synthesis cycle, simple process and easy industrialization.
【技术实现步骤摘要】
一种ZSM-5分子筛及其制备方法
本专利技术涉及分子筛合成领域，特别是涉及一种ZSM-5分子筛的制备方法。
技术介绍
ZSM-5分子筛由Mobil公司首次于上世纪七十年代成功合成，从此之后，因为其特别的择形催化功能和高催化活性，吸引了众多研究者对其进行深入广泛的研究。ZSM-5分子筛的晶粒尺寸有微米级和纳米级，一般把平均晶粒尺寸小于300nm的分子筛定义为纳米ZSM-5分子筛。纳米ZSM-5分子筛的孔道结构与传统微米级ZSM-5分子筛几乎完全相同，但纳米ZSM-5分子筛具有更小的晶粒尺寸、更大的比表面积、更短的孔道和更高的晶内扩散速率等优势，其主要特点如下：(1)由于平均晶粒尺寸的大幅度减小，纳米ZSM-5分子筛的外比表面积更大，暴露的分子筛骨架中的铝原子更多，外表面活性位数量增多,反应活性更高。(2)纳米ZSM-5分子筛使更多的晶胞分散在分子筛外部，使晶粒上具有更多的孔口，可使反应物和产物分子容易进出分子筛孔道。对于反应物和/或产物分子尺寸与分子筛孔口尺寸相当的反应更有利。(3)纳米ZSM-5分子筛...
【技术保护点】
1.一种ZSM-5分子筛的制备方法，包括如下步骤：/na)把铝源、碱源和总用水量的一部分水混合，再加入模板剂混合；/nb)加入硅源，在100℃～120℃下搅拌晶化；/nc)加入剩余水在150℃～180℃下继续晶化获得ZSM-5分子筛。/n
【技术特征摘要】
1.一种ZSM-5分子筛的制备方法，包括如下步骤：
a)把铝源、碱源和总用水量的一部分水混合，再加入模板剂混合；
b)加入硅源，在100℃～120℃下搅拌晶化；
c)加入剩余水在150℃～180℃下继续晶化获得ZSM-5分子筛。
2.根据权利要求1所述的制备方法，其特征在于，步骤a)中，所述铝源选自偏铝酸钠和拟薄水铝石中的一种或两种。
3.根据权利要求1所述的制备方法，其特征在于，所述碱源为氢氧化钠。
4.根据权利要求1所述的制备方法，其特征在于，所述硅源为硅胶颗粒。
5.根据权利要求1所述的制备方法，其特征在于，SiO2：Al2O3：模板剂：Na2O：H2O的摩尔比1:(0.003～0.040):(0.050～0.600):(0.030～0.150):(7～...
【专利技术属性】
技术研发人员：吴勇军，胡治军，杨文书，
申请(专利权)人：惠生工程中国有限公司，
类型：发明
国别省市：上海;31