The invention relates to the technical field of inorganic salt crystallization, in particular to a preparation method of ammonium persulfate crystallization. By controlling the cooling rate and adding the temperature of ammonium persulfate seed, the growth rate of ammonium persulfate crystal is guaranteed to be far greater than the nucleation rate, and then the granular ammonium persulfate crystal is obtained, with uniform particle size distribution, high crystallinity and good fluidity, which is conducive to the compatibility with other materials in practical application, and is not easy to be affected by caking during storage and transportation. Use. In addition, the method provided by the invention has the characteristics of simple operation and low requirement for equipment, and can save process cost.
【技术实现步骤摘要】
一种过硫酸铵结晶体的制备方法
本专利技术涉及无机盐结晶
，具体涉及一种过硫酸铵结晶体的制备方法。
技术介绍
过硫酸铵是无色单斜结晶或白色粉末状结晶，易溶于水，在温水中其溶解度增高。干燥的过硫酸铵具有良好的稳定性，在潮湿空气中易受潮结块。过硫酸铵在化工、轻工、电子、石油及食品工业等领域有着广泛的用途，如广泛用于氯乙烯化合物的聚合引发剂，特别是用于乳化聚合和氧化还原聚合；广泛用于金属的清洗缓蚀剂，特别是用于生产线路板铜的蚀刻；还可用于石油开采的压裂剂、纺织物的脱浆剂、苯胺染料的氧化剂、橡胶硫化剂、蛋白试剂、钢铁分析试剂、肥皂和脂肪的漂白、面粉的熟化剂以及毛发漂白剂等。随着过硫酸铵用途的不断开发研究，行业内对过硫酸铵的要求越来越高，但现有的过硫酸铵粉末普遍存在粒径小、流动性差的缺陷。
技术实现思路
本专利技术的目的在于提供一种过硫酸铵结晶体的制备方法，本专利技术提供的过硫酸铵结晶体的粒径大，流动性好。为了实现上述专利技术目的，本专利技术提供以下技术方案：本专利技术提供了一种过硫酸铵结晶体的制备方法，包括以下步骤：提供过硫酸铵和硫酸铵的混合料液，所述混合料液中过硫酸铵和...
【技术保护点】
1.一种过硫酸铵结晶体的制备方法，包括以下步骤：提供过硫酸铵和硫酸铵的混合料液，所述混合料液中过硫酸铵和硫酸铵的质量浓度比为1：(2～3)；控制所述混合料液的温度为20～25℃时加入过硫酸铵晶种，然后以5～15℃/h降温速率降温至‑2～‑6℃，得到过硫酸铵结晶体。
【技术特征摘要】
1.一种过硫酸铵结晶体的制备方法，包括以下步骤：提供过硫酸铵和硫酸铵的混合料液，所述混合料液中过硫酸铵和硫酸铵的质量浓度比为1：(2～3)；控制所述混合料液的温度为20～25℃时加入过硫酸铵晶种，然后以5～15℃/h降温速率降温至-2～-6℃，得到过硫酸铵结晶体。2.根据权利要求1所述的制备方法，其特征在于，所述混合料液中过硫酸铵的浓度为180～220g/L。3.根据权利要求1所述的制备方法，其特征在于，所述混合料液的pH值为7.0～8.0。4.根据权利要求1所述的制备方法，其特征在于，所述降温的过程在搅拌条件下进行，所述搅拌的速率为30～40r/min。5.根据权利要求1所述的制备方法，其特征在于，所述过硫酸铵晶种的粒径为60目以下。6.根据权利要求5所述的制备方法，其特征在于，当所述过硫...
【专利技术属性】
技术研发人员：高毅颖，郭强，王洋洋，王硕，贾志军，李达，
申请(专利权)人：河北中科同创科技发展有限公司，中国科学院过程工程研究所，
类型：发明
国别省市：河北,13