The invention relates to the technical field of electric vacuum technology. The invention discloses a turning process of ZGMn13 for electric vacuum, which includes: turning heat treatment process: heating high manganese steel ZGMn13 material to 650 700 C before rough processing, holding for 3 5 h and cooling; quenching before finishing and use of workpiece, quenching is carried out at a heating rate of less than 80 C/h to raise the temperature of high manganese steel ZGMn13 material to 650 700 C before rough processing. 1040 1089 The processing quality and efficiency of the product have been greatly improved by this process. The product has been applied in many products, such as traveling wave tube, klystron, magnetron and so on, with good results.
【技术实现步骤摘要】
一种电真空用ZGMn13的车削加工工艺
本专利技术涉及电真空工艺
，尤其涉及一种电真空用ZGMn13的车削加工工艺。
技术介绍
ZGMn13是一种在行波管、速调管等的磁场结构中常用的无磁不锈钢材料。而无磁不锈钢具有的特殊性质使得磁力线可以穿过，因而在某些真空微波器件中有重要的应用，其在脉冲磁场下产生的涡流损耗相对于铜或者其他金属要小一些，这是由于无磁不锈钢的电导率小于铜。ZGMn13主要有ZGMn13—1(C含量1.10％～1.50％)、ZGMn13—2(C含量1.00％～1.40％)、ZGMn13—3(C含量0.90％～1.30％)、ZGMn13-4(C含量0.90％～1.20％)四种牌号。以上4种牌号钢的锰含量均为11.0％～14.0％。高锰钢ZGMn13易加工硬化，原因是在冲击载荷作用的冷变形过程中，由于位错密度大量增加，位错的交割、位错的塞积及位错和溶质原子的交互作用使钢得到强化。另一个重要原因则是高锰奥氏体的层错能低，形变时容易出现堆垛层错，从而为ε马氏体的形成和形变孪晶的产生创造了条件，而ε马氏体和形变孪晶的出现使钢难以变形，尤其是后者的作用更大...
【技术保护点】
1.一种电真空用ZGMn13的车削加工工艺，其特征在于，包括：车削热处理工艺：在粗加工前，将高锰钢ZGMn13材料加热到650‑700℃，保温3‑5h后冷却；在工件精车和使用前，进行淬火，淬火是以≤80℃/h升温速度，将高锰钢ZGMn13材料升温至1040‑1060℃，保温2.5‑3.5h，然后在5min内升温到1090‑1110℃，保温20‑40min出炉，出炉后在45s时间内入水冷却。
【技术特征摘要】
1.一种电真空用ZGMn13的车削加工工艺，其特征在于，包括：车削热处理工艺：在粗加工前，将高锰钢ZGMn13材料加热到650-700℃，保温3-5h后冷却；在工件精车和使用前，进行淬火，淬火是以≤80℃/h升温速度，将高锰钢ZGMn13材料升温至1040-1060℃，保温2.5-3.5h，然后在5min内升温到1090-1110℃，保温20-40min出炉，出炉后在45s时间内入水冷却。2.根据权利要求1所述的加工工艺，其特征在于，高锰钢ZGMn13材料入水时，水温应控制在≤30℃，淬火后，水温应控制在≤50℃，水量应不小于淬火材料重量的8倍。3.根据权利要求1或2所述的加工工艺，其特征在于，车削加工时切削速度为20-40m/min。4.根据权利要求1-3任一项所述的加工工艺，其特征...
【专利技术属性】
技术研发人员：江祝苗，
申请(专利权)人：安徽新芜精密装备制造产业技术研究院有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。