A ferrous thermistor consists of 30 parts of Mn3O4 (manganese oxide), 5 to 30 parts of Fe2O3 (iron oxide), 12 to 20 parts of Ni2O3 (nickel oxide), 8 to 30 parts of CuO (copper oxide), 2 to 8 parts of Al2O3 (aluminium oxide), and 2 to 8 parts of SiO 2 (silicon dioxide). After mixing operation, wet grinding operation, mixing granulation operation, dry pressure operation, pre-sintering operation, post-sintering operation, silver paste coating operation, heat treatment operation and ripening operation, the components of the iron-containing thermistor of the invention can obtain the iron-containing thermistor. According to the experimental results, the resistivity of the iron-containing thermistor is 180-320 (_.mm), and the iron-containing thermistor is thermistor. The B value of resistance is 1800K-2250K, which has the characteristics of low resistivity, small B value and high overall stability.
【技术实现步骤摘要】
含铁系热敏电阻及其制备方法
本专利技术涉及一种热敏电阻，特别是涉及一种含铁系热敏电阻及其制备方法。
技术介绍
负温度系数热敏电阻材料，又称NTC热敏电阻材料，是一类电阻随温度升高而减小的传感器电阻材料，广泛用于我国工业生产、科研、航空和军事装备领域。然而在实际使用过程中，对于不同的应用温度，不同的使用电路等，需要该负温度系数(NTC)热敏电阻具有不同的标准电阻(25℃电阻)和材料常数(B值)。通常传统的NTC热敏电阻陶瓷材料一般由锰、钴、镍等过渡金属的氧化物组成，这类热敏材料B值高，其电阻率高。而在实际应用中，常常需要采用低B值及低电阻率的负温度系数热敏电阻材料，而在现有的负温度系数热敏电阻材料中加入铁元素能够使NTC热敏电阻达到低B值与低电阻率的要求，因此，如何将铁元素应用在NTC热敏电阻上，使得NTC热敏电阻达到低B值与低电阻率的要求是本领域研发人员需要解决的问题。
技术实现思路
本专利技术的目的是克服现有技术中的不足之处，提供一种采用添加铁元素使得NTC热敏电阻的能够达到低B值与低电阻率的要求的含铁系热敏电阻及其制备方法。含铁系热敏电阻本专利技术的目的是通过以下...
【技术保护点】
1.一种含铁系热敏电阻，其特征在于，包括如下质量份的各组分：
【技术特征摘要】
1.一种含铁系热敏电阻，其特征在于，包括如下质量份的各组分：其中，所述含铁系热敏电阻的电阻率为180～320(Ω·mm)，所述含铁系热敏电阻的B值为1800K～2250K。2.根据权利要求1所述的含铁系热敏电阻，其特征在于，包括如下质量份的各组分：3.根据权利要求1所述的含铁系热敏电阻，其特征在于，包括如下质量份的各组分：4.根据权利要求1所述的含铁系热敏电阻，其特征在于，包括如下质量份的各组分：5.一种含铁系热敏电阻含铁系热敏电阻的制备方法，其特征在于，包括如下步骤：将Mn3O4、Fe2O3、Ni2O3、CuO、Al2O3和SiO2混合，并进行湿式研磨操作，得到研磨混料；其中，Mn3O4、Fe2O3、Ni2O3、CuO、Al2O3和SiO2的质量比例为30：(5～30)：(12～20)：(8～30)：(2～8)：(2～8)；对所述研磨混料进行烘干操作后，再加入粘合剂进行混料成粒操作，得到混料颗粒；将所述混料颗粒进行干压操作，得到干压片体；在650℃～830℃的温度条件下...
【专利技术属性】
技术研发人员：张少钰，
申请(专利权)人：惠州嘉科实业有限公司，
类型：发明
国别省市：广东,44