The invention relates to a molybdenum carbide nanosheet and its preparation method and application. The method comprises mixing molybdenum source, ammonium nitrate and glycine evenly, then heating to 160-180 degrees C to obtain mixture 1, adding glucose, then heating to 230-280 degrees C to obtain fluffy solid, heating to 450-550 degrees C in hydrogen atmosphere, and cooling to obtain molybdenum carbide nanosheet. The preparation method of molybdenum carbide nanosheet has the advantages of low heating temperature, easy operation and popularization, no agglomeration, irregular sheet shape and large specific surface area, and excellent catalytic performance in the application of electrocatalytic hydrogen production.
【技术实现步骤摘要】
一种碳化钼纳米片及其制备方法和应用
本专利技术涉及碳化钼制备方法，尤其是一种碳化钼纳米片及其制备方法和应用。
技术介绍
氢能的利用是传统化石能源是佳的可替代绿色能源，而氢能的利用取决于制氢技术的发展。电解水制氢技术为行业誉为“最理想的工业制氢方法”，该技术的最核心问题是高效、稳定、廉洁的制备电催化剂的开发。目前，铂基催化剂是最为有效的电催化剂，但其高昂的成本和低存储量严重制约了该类催化剂的广泛应用。碳化钼(Mo2C)由于具有类贵金属性质、耐焙烧、耐硫耐氮、高熔点等优点，在催化领域中得到了广泛的关注，成为最具有潜力代替贵金属Pt、Pd的催化材料之一。目前，碳化钼的制备方法主要有化学气相沉积法、程序升温还原法和碳热氢还原法。化学气相沉积法可制备出高比表面、高质量的薄膜Mo2C催化剂，但该方法的沉积效率比较低。程序升温还原法可制备纳米Mo2C催化剂，同时具有较高的活性，但该方法需要复杂和严格的合成条件，可控性较差。碳热氢还原法通过控制活性组分和温度可合成高比表面积、晶粒大小可控的高性能Mo2C催化剂。原料方面，碳源是合成高性能Mo2C的关键之一，不同的碳源可合成不同晶体...
【技术保护点】
1.一种碳化钼纳米片的制备方法，其特征在于：包括以下步骤：步骤1：将钼源、硝酸铵、甘氨酸混合均匀，之后加热到160～180℃，得到混合物1；步骤2：向步骤1得到的混合物1中加入葡萄糖，之后加热到230～280℃，获得蓬松固体；步骤3：将步骤2得到的蓬松固体放入氢气氛围下加热到450～550℃，降温得到碳化钼纳米片。
【技术特征摘要】
1.一种碳化钼纳米片的制备方法，其特征在于：包括以下步骤：步骤1：将钼源、硝酸铵、甘氨酸混合均匀，之后加热到160～180℃，得到混合物1；步骤2：向步骤1得到的混合物1中加入葡萄糖，之后加热到230～280℃，获得蓬松固体；步骤3：将步骤2得到的蓬松固体放入氢气氛围下加热到450～550℃，降温得到碳化钼纳米片。2.根据权利要求1所述的碳化钼纳米片的制备方法，其特征在于：步骤1中所述钼源为仲钼酸铵、四钼酸铵或二钼酸铵中至少一种；任选的，步骤1中所述钼源中钼的摩尔的量：(所述硝酸铵的摩尔的量+甘氨酸的摩尔的量)＝0.5～1.0:2.2～3.2；任选的，步骤1中所述硝酸铵的质量：所述甘氨酸的质量＝0.8～3.2。3.根据权利要求2所述的碳化钼纳米片的制备方法，其特征在于：步骤1包括：1a将钼源、硝酸铵、甘氨酸混合后加入去离子水，搅拌至溶解；1b加热溶液到165～175℃，保温3～6分钟，得到混合物1。4.根据权利要求1所述的碳化钼纳米片的制备方...
【专利技术属性】
技术研发人员：古思勇，张厚安，陈伟斌，周洪涛，
申请(专利权)人：厦门理工学院，
类型：发明
国别省市：福建,35