The invention relates to a fluorinated acrylic copolymer surface treating agent, which belongs to the surface treatment agent technology field. The treatment agent includes 10 acrylonitrile 15, 10 methacrylic isooctyl methacrylic acid 5, 10 methacrylic acid isoamyl 15, twelve methacrylic acid twelve 5, 3 hydroxypropyl acrylate 3, 5, propylene epoxypropyl acrylate 10, azo nitrile acrylonitrile, methyl acrylic acid, fluoro butyl acrylate, silane coupling agent. 570, 0.5, 1, xylene 80, 100, two lauric acid two butyltin 0.5, 1. The fluorinated acrylate monomer modified styrene acrylic copolymer has high bonding strength, surface hardness, abrasion resistance and washability. The fluorinated acrylate modified styrene acrylic copolymer surface treatment agent has excellent surface properties and can be applied to surface treatment of cement concrete and ceramics.
【技术实现步骤摘要】
一种含氟丙烯酸共聚物表面处理剂
本专利技术涉及一种表面处理剂，更具体地说，本专利技术涉及一种含氟丙烯酸共聚物表面处理剂，属于表面处理剂
技术介绍
丙烯酸酯类聚合物具有优异的光稳定性、耐候性以及良好的耐水、耐碱、耐化学品、耐热和耐寒性等，但其表面能较大，憎水避水效果不佳。有机氟化合物中氟原子的电负性大，材料表面具有较低的表面能，可使水的表面张力显著降低；同时，与氢原子相比，氟原子的化学惰性可使材料保持高度的稳定性。国家知识产权局于2006.06.07公开了一件公开号为CN1784480A，名称为“含有含氟聚合物的表面处理剂”的专利技术，该专利技术一种含有含氟聚合物的表面处理剂，其中所述含氟聚合物具有：(A)由下述通式(I)表示的含氟单体衍生的重复单元、(B)由不含氟原子的单体衍生的结构单元、以及(C)根据需要存在的由交联性单体衍生的结构单元。所述表面处理剂中，即使含氟聚合物的侧链为碳原子数小于等于4的短链氟代烷基，该表面处理剂仍具有优异的防水性、防油性、防污性。
技术实现思路
本专利技术旨在解决现有技术中的含氟丙烯酸共聚物表面处理剂粘结强度、表面硬度、耐磨性和...
【技术保护点】
一种含氟丙烯酸共聚物表面处理剂，其特征在于：包括以下按照重量份数计的原料：丙烯腈 10‑15份甲基丙烯酸异辛酯 5‑10份甲基丙烯酸异戊酯 10‑15份甲基丙烯酸十二酯 5‑10份丙烯酸羟丙酯 3‑5份丙烯酸环氧丙酯 10‑15份偶氮二异丁腈 1‑3份甲基丙烯酸六氟丁酯 ...
【技术特征摘要】
1.一种含氟丙烯酸共聚物表面处理剂，其特征在于：包括以下按照重量份数计的原料：丙烯腈10-15份甲基丙烯酸异辛酯5-10份甲基丙烯酸异戊酯10-15份甲基丙烯酸十二酯5-10份丙烯酸羟丙酯3-5份丙烯酸环氧丙酯10-15份偶氮二异丁腈1-3份甲基丙烯酸六氟丁酯10-15份硅烷偶联剂KH-5700.5-1份二甲苯80-100份二月桂酸二丁基锡0.5-1份。2.根据权利要求1所述的一种含氟丙烯酸共聚物表面处理剂，其特征在于：包括以下按照重量份数计的原料：丙烯腈12-14份甲基丙烯酸异辛酯8-10份甲基丙烯酸异戊酯12-13份甲基...
【专利技术属性】
技术研发人员：张一帆，
申请(专利权)人：成都锦汇科技有限公司，
类型：发明
国别省市：四川,51