The invention provides a preparation method of porous polyacrylonitrile. The method comprises the following steps: (1) aqueous preparation: polyvinylpyrrolidone, deionized water, transparent solution; (2) the oil phase preparation: acrylonitrile, crosslinking agent, organic photoinitiators, atom transfer radical initiator was mixed, oil phase; (3) the the water under the condition of stirring slowly added to the oil phase, adding after light polymerization at room temperature, after postprocessing, porous polyacrylonitrile. The invention adopts light irradiation polymerization, which has simple operation and low cost, and the pore size of porous polyacrylonitrile is uniform and has a larger specific surface area.
【技术实现步骤摘要】
一种多孔聚丙烯腈的制备方法
本专利技术属于高分子材料合成领域，具体是一种多孔聚丙烯腈的制备方法。
技术介绍
：多孔材料广泛用于分离膜、吸附剂、气体储存媒介、催化剂载体和组织工程支架等领域。孔尺寸及分布、孔隙率、孔壁的表面化学性能以及孔结构决定了多孔材料的性质和功能，发展简单高效的制备规整有序多孔结构的方法一直以来都是研究的重点。原子转移自由基聚合（atomtransferradicalpolymerization，ATRP）是九十年代发展起来的一种活性聚合技术，有着重要应用价值。1995年，美国卡耐基－梅隆大学的王锦山博士、K·Matyjaszewski教授[Controlled/livingradicalpolymerization.atomtransferradicalpolymerizationinthepresenceoftransition-metalcomplexes,JAmChemSoc,1995,117,5614-5615.]以及日本京都大学的泽本光南教授[Polymerizationofmethylmethacrylatewiththecarbo...
【技术保护点】
一种多孔聚丙烯腈的制备方法；其特征在于：（1）水相的制备：将聚乙烯吡咯烷酮、去离子水混合，得到透明溶液；（2）油相的制备：将丙烯腈、交联剂、有机光引发剂、原子转移自由基聚合引发剂，得到油相；（3）将所得的水相在搅拌状态下缓慢的加入到油相中，滴加完毕以后，通氮除氧，室温下光照，进行聚合反应；反应结束后，经过后处理，制得孔径均匀、较大比表面积的多孔聚丙烯腈。
【技术特征摘要】
1.一种多孔聚丙烯腈的制备方法；其特征在于：（1）水相的制备：将聚乙烯吡咯烷酮、去离子水混合，得到透明溶液；（2）油相的制备：将丙烯腈、交联剂、有机光引发剂、原子转移自由基聚合引发剂，得到油相；（3）将所得的水相在搅拌状态下缓慢的加入到油相中，滴加完毕以后，通氮除氧，室温下光照，进行聚合反应；反应结束后，经过后处理，制得孔径均匀、较大比表面积的多孔聚丙烯腈。2.根据权利要求1所述的有机光引发剂，其特征在于所述的有机光引发剂为苝、3,4,9,10-四（12-烷氧羰基）苝、吩噻嗪、5,10-二苯基-5,10-二氢吩噻嗪、3,7-二溴-N-甲基吩噻嗪。3.根据权利要求...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。