The invention discloses a production method of quick remedial material, including the following steps: (1) batching: dolomite clinker, magnesia fine powder, pulverized coal, metal aluminum powder and iron oxide powder; (2) mixing the raw material through mixing machine to get a mixture of 4.8 moisture content 5.2% (percentage of weight per weight); (3) roasting reduction: (3) The mixture is loaded into the reaction tank, the reaction tank is sealed to cut off the air, roasted and reduced in the high temperature heating room, and the temperature of the high temperature heating room is 1000 1200 degrees C; (4) drying: the mixture is dried in a loose material dryer and dry, after drying, a loose, dry and uniform remedial material is obtained. The production method adopted by the invention significantly improves the metallization rate of the burden, meets the production requirements, has simple operation, low cost and saves the cost of steelmaking.
【技术实现步骤摘要】
一种快速补炉料的生产方法
本专利技术属于炉炼钢
，尤其涉及一种快速补炉料的生产方法。
技术介绍
转炉是炼钢的主要冶炼容器，其炉龄直接影响着炼钢的生产组织，因此转炉炉龄是衡量转炉炼钢的一项综合性技术经济指标。但随着转炉冶炼强度及生产节奏的大幅度提高,对维护转炉用补炉料的质量要求也越来越苛刻。转炉前后大面侵蚀过快已成为影响转炉炉龄提高的关键因素。因此，加强转炉前后大面维护，以使炉衬达到均衡侵蚀，降低耐火材料消耗，对于进一步提高转炉炉龄具有十分重要的意义。
技术实现思路
本专利技术的目的是提供一种快速补炉料的生产方法，为克服上述现有技术的不足，本专利技术解决现有感应炉无法补炉的问题，缩短修炉时间，延长炉衬寿命，节约炼钢成本，同时，加快护炉料输送速度，提高护炉效率和效果，延长炉缸使用周期。为了达到上述目的，本专利技术采用以下技术方案实现：一种快速补炉料的生产方法，包括以下步骤：(1)配料：白云石熟料、镁砂细粉、煤粉、金属铝粉和氧化铁粉，按质量百分数计算，具体的配比为：白云石熟料20-40％镁砂细粉3-5％煤粉2-6％金属铝粉10-30％氧化铁粉40-50％；(2)混匀：...
【技术保护点】
一种快速补炉料的生产方法，包括以下步骤：(1)配料：白云石熟料、镁砂细粉、煤粉、金属铝粉和氧化铁粉，按质量百分数计算，具体的配比为：白云石熟料20‑40％镁砂细粉3‑5％煤粉2‑6％金属铝粉10‑30％氧化铁粉40‑50％；(2)混匀：将上述原料经混料机混匀，得到含水率为4.8‑5.2％(按重量百分比计)的混合料；(3)焙烧还原：将上述混合料装入反应罐中，将反应罐密封以隔绝空气，在高温加热室中焙烧还原，控制高温加热室的温度为1000‑1200℃；(4)干燥：将混合物放入松散物料干燥机内干燥，干燥后即得松散、干状、均匀的补炉料。
【技术特征摘要】
1.一种快速补炉料的生产方法，包括以下步骤：(1)配料：白云石熟料、镁砂细粉、煤粉、金属铝粉和氧化铁粉，按质量百分数计算，具体的配比为：白云石熟料20-40％镁砂细粉3-5％煤粉2-6％金属铝粉10-30％氧化铁粉40-50％；(2)混匀：将上述原料经混料机混匀，得到...
【专利技术属性】
技术研发人员：狄崇振，刘冰，狄崇高，周梅，曾庆军，
申请(专利权)人：徐州市伟华炉料有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。