A method for improving the cold heading performance of graphitization of easy cutting steel belongs to the field of steel material processing technology. It is characterized by using warm deformation technology to degrade graphitized graphitized free cutting steel wire rod by dynamic recrystallization of ferrite, and improve the cold heading performance of graphitized free cutting steel by controlling the refinement and homogenization of ferrite grains. The specific method is through the graphitization of graphite free cutting steel wire is heated to 550~710 DEG C, the temperature of the elongation is 18 ~ 38% of rolling, rolling after cooling to room temperature. The graphitized free cutting steel processed by this method is refined and even, and the cold heading performance is improved obviously. It can achieve small head forging ratio, and the specimen does not produce any visible defects such as cracks and folding.
【技术实现步骤摘要】
一种提高石墨化易切削钢冷镦性能的方法
本专利技术涉及一种提高石墨化易切削钢冷镦性能的方法，属于钢铁材料加工
技术介绍
石墨化易切削钢盘条的制备流程主要是由炼钢、浇注、热轧、石墨化处理等工艺过程组成。其中，盘条经石墨化处理后，表现出较高的冷成形和切削性能，具有较低的屈强比，能够软化到与低碳钢一样的水平，不仅具有良好的切削性能，还具有很高的冷镦性能。经石墨化处理的盘条，其组织主要由铁素体+石墨组成。然而，由于石墨化处理过程需要的时间较长，往往导致盘条中的铁素体组织粗大，且不均匀，这势必对其冷镦性能产生不利影响。目前，石墨化易切削钢，其冷镦前不对铁素体组织进行细化的处理，即石墨化处理后，进行切削、冷镦，如IwamotoTakashi.MurakamiToshiyuki在JFETechnRep(2004，(4)：64-69)上发表的论文“BarandWireSteelsforGearandValveofAutomobile(Eco-FriendlyFreeCuttingSteelwithoutLeadAddition)”。因此，为解决现有石墨化处理方法中存在的铁...
【技术保护点】
一种提高石墨化易切削钢冷镦性能的方法，其特征在于利用温变形技术，对石墨化处理后的石墨化易切削钢盘条进行铁素体动态再结晶的温变形，以实现铁素体晶粒的细化和均匀化；具体方法是将经过石墨化处理的石墨化易切削钢盘条加热到550～710℃，待均温后进行延伸率为18～38％的孔型轧制，轧后空冷至室温。
【技术特征摘要】
1.一种提高石墨化易切削钢冷镦性能的方法，其特征在于利用温变形技术，对石墨化处理后的石墨化易切削钢盘条进行铁素体动态再结晶的温变形，以实现铁素体晶粒的细化和均匀化；具体方法是将经过石墨化处理的石墨化易切削钢盘条加热到550～710℃，待均温后进行延伸率为18～38％的孔型轧制，轧后空冷至室温。2.据权利要求1所述的一种提高石墨化易切削钢冷镦性能的方法，其特征在于，所述的石墨化处理，是指对石墨化易切削钢盘条在温度为600...
【专利技术属性】
技术研发人员：张永军，张鹏程，于文杰，王九花，韩静涛，
申请(专利权)人：北京科技大学，
类型：发明
国别省市：北京,11
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。