The present invention provides a method for preparing a melt in situ control of aluminum matrix composites, which includes the following steps: pure aluminum or Aluminum Alloy matrix after melting, adding salt reaction and reaction assistant, blowing the argon and stirring reaction; after the reaction to remove salt slag, refining after casting, i.e.. The preparation method solves the problem that the size and distribution of the reinforced phase of the aluminum matrix composite TiB2 and the settlement deflection are controlled. The aluminum matrix composites with TiB2 content up to 15%wt and homogeneous structure and excellent properties were prepared, which also provided a basis for further development and application of particle reinforced composites prepared by mixed salt reaction.
【技术实现步骤摘要】
熔体控制自生铝基复合材料的制备方法
本专利技术属于复合材料领域，涉及一种制备铝基复合材料的方法，具体地，涉及一种熔体控制自生铝基复合材料的制备方法。
技术介绍
近年来，许多文章报导了关于原位自生反应颗粒增强铝基复合材料的研究。其特点是：增强颗粒在基体内部原位合成,基体界面结合较好且界面干净；原位增强颗粒尺寸细小(一般<3.0μm)且在基体中分布均匀；通过选择反应类型及控制反应参数,可获得不同种类、不同数量的原位增强颗粒；增强颗粒的原位合成同铸造技术结合起来；工艺简便、成本低；可用来制备一定形状和大小的复合材料。经文献检索发现，DaciesP.DevelopmentofCastAluminiumMMCs(铝基复合材料的发展)，KeyEngineeringMaterials(重要工程材料)，1993,77:357-362，但该方法存在着所制备的复合材料中增强相颗粒尺寸和分布不均匀；且质量分数不高，或当TiB2质量分数大于8wt％时，其组织结构恶化，铸造性能变差，材料的力学性能大大降低。如何采用合理的工艺有效控制增强相的尺寸、分布以及沉降偏聚一直未见有报导...
【技术保护点】
一种熔体控制自生铝基复合材料的制备方法，其特征在于，包括如下步骤：将纯铝或铝合金基体熔化后，加入反应盐和反应助剂，吹入氩气并搅拌，反应；反应完成后清除盐渣，进行精炼处理后浇铸，即得。
【技术特征摘要】
1.一种熔体控制自生铝基复合材料的制备方法，其特征在于，包括如下步骤：将纯铝或铝合金基体熔化后，加入反应盐和反应助剂，吹入氩气并搅拌，反应；反应完成后清除盐渣，进行精炼处理后浇铸，即得。2.根据权利要求1所述的熔体控制自生铝基复合材料的制备方法，其特征在于，所述反应助剂包括质量比为2:1:1～4:1:1的Na3AlF6、LiF3、LiCl3。3.根据权利要求1所述的熔体控制自生铝基复合材料的制备方法，其特征在于，所述反应盐包括质量比为1:1～2:1的NaBF4和Na2TiF6。4.根据权利要求1所述的熔体控制自生铝基复合材料的制备方法，其特征在于，所述反应助剂的加入量为反应盐的5-15wt％。5.根据权利要求1所述的熔体控制自生铝基复合材料的制备方法，其特...
【专利技术属性】
技术研发人员：李险峰，王浩伟，马乃恒，陈东，张亦杰，夏存娟，
申请(专利权)人：上海交通大学，
类型：发明
国别省市：上海,31