The invention discloses a method for preparing graphene Aluminum Alloy profile, which comprises the following steps: (1) will use Shi Moxi and aluminum ball mill for grinding, composite particles made of graphene and aluminum, composite particle size is 3 5mm; (2) the composite sheet can be compacted into 0.5 1mm; (3) the Aluminum Alloy ingot heating melt into a liquid, and stirring the liquid aluminum; (4) the step (2) was added to the plates to step (3) in liquid aluminum, and keep stirring 0.5 1 hours; and then the liquid aluminum casting, graphite graphene aluminum alloy profile; in graphene Aluminum Alloy profiles, weight percentage of graphene was 1 3%; the thickness of graphene is 5 10nm, graphene sheet size is 2 20 micron. This method can well disperse Shi Moxi into the matrix of aluminum alloy and form a stable dispersion system.
【技术实现步骤摘要】
一种石墨烯铝合金型材的制备方法
本专利技术涉及一种石墨烯铝合金型材的制备方法。
技术介绍
铝合金是目前应用量较为广泛的金属结构材料之一，其具有良好的导热性能，同时由于其比重小，可塑性强，加工性能优良，价格便宜，被广泛应用于空调散热片、计算机散热器、LED模块散热件等领域。然而随着电子科学技术的发展对各类散热器件的散热性能要求越来越高，在能满足易加工成型的基础上，尽量提高其热物理性能。其中石墨烯就一种很好的增强相，石墨烯是一种完美的sp2杂化的一维碳材料，理论计算显示其具有超高的热导率(5000-6000W/m.K)及力学性能，为引领新材料发展进入了全新的视角。但是如何将石墨烯均匀地分散到铝基体中，目前常用的方法是直接将石墨烯投入到熔融的铝液中，然后浇注得到含有石墨烯的铝合金型材，但是由于石墨烯为粉末状，且由于石墨烯和铝的润湿性较差，在投入到铝液中后，即使采用搅拌，但由于铝液的粘度极大，石墨烯在铝液中仍难以分散均匀，部分石墨烯会形成团聚，使型材性能的均一性下降。
技术实现思路
本专利技术的目的在于提供一种石墨烯铝合金型材的制备方法，该方法能够很好地使石墨烯均匀分散到铝合...
【技术保护点】
一种石墨烯铝合金型材的制备方法，其特征在于，包括如下步骤：(1)将石墨烯和铝粉利用球磨机进行研磨，制成石墨烯和铝粉的复合颗粒，复合颗粒的粒径为3‑5mm；(2)将复合可以碾压为0.5‑1mm的片体；(3)将铝合金锭加热融化为液态，成为铝液，并搅拌；(4)将步骤(2)所制得的片体加入到步骤(3)中的铝液中，并保持搅拌0.5‑1小时；然后将铝液进行浇注，得到石墨烯铝合金型材；在石墨烯铝合金型材中，石墨烯的重量百分比为1‑3％；所述石墨烯的厚度为5‑10nm，石墨烯的片径为2‑20微米。
【技术特征摘要】
1.一种石墨烯铝合金型材的制备方法，其特征在于，包括如下步骤：(1)将石墨烯和铝粉利用球磨机进行研磨，制成石墨烯和铝粉的复合颗粒，复合颗粒的粒径为3-5mm；(2)将复合可以碾压为0.5-1mm的片体；(3)将铝合金锭加热融化为液态，成为铝液，并搅拌；(4)将步骤(2)所制得的片体加入到步骤(3)中的铝液中，并保持搅拌0.5-1小时；然后将铝液进行浇注，得到石墨烯铝合金型材；在石墨烯铝合金型材中，石墨烯的重量百分比为1-3％；所述石墨烯的厚度为5-10nm，石墨烯的片径为2-20微米。2....