The present invention is to provide a glass cover local thinning process, comprising the following steps: 1) in the concave groove surface of the glass cover and other parts without etching with acid proof ink; 2) the glass cover into the mold, the mold is etched to supply hydrofluoric acid etching, reach the requirements will cover glass in lye 3); in alkaline wash acid ink on the cover glass; 4) the glass cover is placed into water rinse, and then air dried; 5) to detect the local glass cover thickness reduction is qualified; 6) again after cleaning, get the local reduction of thin glass cover. The invention is etched with chemical method, and the operation is simple and efficient, and it has no dust after etching and easy to clean.
【技术实现步骤摘要】
一种玻璃盖板局部减薄工艺
本专利技术属于玻璃板精细加工领域,具体涉及一种玻璃盖板局部减薄工艺。
技术介绍
玻璃材质一直以其晶莹透亮的特性受到设计师的青睐。而随着交互式技术的不断发展,也使得玻璃板更为广泛的应用到了IT产品的设计中。玻璃板为平面结构,如果要实现凸凹槽、各类孔等,使用物理方法容易使玻璃板破碎,成功率低并且加工难度大,加工后有粉尘,难以清洁。目前有人采用化学方法对玻璃板进行切割,但因为化学方法蚀刻工艺对玻璃板加工的精度控制较难,减薄的均匀性以及厚度于所需的精准数据有较大误差,所以化学方法对玻璃板进行减薄的工艺还没有开展。
技术实现思路
针对现有技术中存在的问题,本专利技术提供一种玻璃盖板局部减薄工艺。为实现本专利技术的目的,本专利技术提供了以下技术方案:一种玻璃盖板局部减薄工艺,步骤包括:1)在玻璃盖板表面的凹凸槽以及其他无需蚀刻的部分涂上耐酸油墨;2)将玻璃盖板放入模具中,向模具内供给氢氟酸溶液进行蚀刻,达到蚀刻要求后将玻璃盖板放入碱液中;3)在碱液中洗净玻璃盖板上的耐酸油墨;4)将玻璃盖板放入清水中冲洗,然后风干;5)检测局部减薄的玻璃盖板厚度是否合格;6)合格后再次清洗,得到局部减薄的玻璃盖板。所述氢氟酸溶液为质量百分比为15-25%。所述氢氟酸溶液还包括质量百分比为2-15%的双氧水。所述在模具内的蚀刻时间为5-10分钟。所述耐酸油墨为酚醛树脂和甲醛树脂的任一种。所述工艺加工玻璃为弧面、大孔、小孔、凹槽及外形倒边的任一种。本专利技术的优点在于:1、本专利技术采用化学方法蚀刻,操作简单效率高,并且蚀刻后无粉尘,易清洁。2、本专利技术的氢氟酸溶液 ...
【技术保护点】
一种玻璃盖板局部减薄工艺,其特征在于:步骤包括:1)在玻璃盖板表面的凹凸槽以及其他无需蚀刻的部分涂上耐酸油墨;2)将玻璃盖板放入模具中,向模具内供给氢氟酸溶液进行蚀刻,达到蚀刻要求后将玻璃盖板放入碱液中;3)在碱液中洗净玻璃盖板上的耐酸油墨;4)将玻璃盖板放入清水中冲洗,然后风干;5)检测局部减薄的玻璃盖板厚度是否合格;6)合格后再次清洗,得到局部减薄的玻璃盖板。
【技术特征摘要】
1.一种玻璃盖板局部减薄工艺,其特征在于:步骤包括:1)在玻璃盖板表面的凹凸槽以及其他无需蚀刻的部分涂上耐酸油墨;2)将玻璃盖板放入模具中,向模具内供给氢氟酸溶液进行蚀刻,达到蚀刻要求后将玻璃盖板放入碱液中;3)在碱液中洗净玻璃盖板上的耐酸油墨;4)将玻璃盖板放入清水中冲洗,然后风干;5)检测局部减薄的玻璃盖板厚度是否合格;6)合格后再次清洗,得到局部减薄的玻璃盖板。2.根据权利要求1所述的玻璃盖板局部减薄工艺,其特征在于:所述氢氟酸溶液为质...
【专利技术属性】
技术研发人员:邓松青,钟朝阳,
申请(专利权)人:东莞市瑞立达玻璃盖板科技股份有限公司,
类型:发明
国别省市:广东,44