The present invention relates to the field of polymer material, and discloses a preparation method of silica gel in the tackifier, which comprises the following steps: a. the hydrogen containing polysiloxane containing vinyl silane in accordance with nH:nVi=2:1 1.5 mixed; chloroplatinic acid catalyst B. with 9 20ppm dosage, reaction temperature control in 50 90 degrees Celsius. 2 hour 1 reaction; C. cooling to room temperature, the inhibitor of hydrogen containing polysiloxane containing vinyl silane with a total weight of 0.5 2%, get the silica gel adhesive products. The said internal viscosity increasing agent is applied to silicone rubber, which greatly increases its adhesion to glass, PET, TPU, aluminum plates and copper plates, and does not affect its fluidity. It has achieved good results in industrial applications.
【技术实现步骤摘要】
一种硅胶内增粘剂的制备方法及其应用
本专利技术涉及高分子材料领域，具体涉及一种硅胶内增粘剂的制备方法及其应用。
技术介绍
加成型硅橡胶是一种无毒无味、具有优良耐候性和电绝缘性的有机硅材料，是近年来发展较快的高档有机硅品种之一，与缩合型硅橡胶比具有硫化过程不产生副产物，收缩率小，能深度硫化等特点，但是，由于加成型硅橡胶自身分子极性低的原因，其固化后与基材粘接性能较差。为提高加成型硅橡胶对所接触材料的粘接性，一般采取添加内增粘剂的方法，然而常见的内增粘剂由于与硅橡胶的相容性或较易与硅橡胶形成氢键，导致添加增粘剂的硅橡胶透明度变差，流动性变差。
技术实现思路
本专利技术所要解决的技术问题是提一种硅胶内增粘剂的制备方法及其应用，克服了现有技术的缺陷，使用时极大增加了硅胶对玻璃，PET,TPU,铝板，铜片粘接力，不影响其流动性。本专利技术所要解决的技术问题通过以下技术方案予以实现：一种硅胶内增粘剂的制备方法，包括如下步骤：a.将含氢聚硅氧烷与含乙烯基硅烷按照nH:nVi=2:1-1.5（即含氢聚硅氧烷的氢基个数与含乙烯基硅烷的乙烯基个数之比）的比例混合；所述含氢聚硅氧烷为至少有...
【技术保护点】
一种硅胶内增粘剂的制备方法，其特征在于，包括如下步骤：a. 将含氢聚硅氧烷与含乙烯基硅烷按照nH:nVi=2:1‑1.5的比例混合；b.加入步骤a总物料重量的9‑20ppm的氯铂酸催化剂，控制反应温度在50‑90摄氏度，反应1‑2小时；c. 降温至室温，加入含氢聚硅氧烷与含乙烯基硅烷总重量0.5‑2%的抑制剂，得到硅胶内增粘剂成品。
【技术特征摘要】
1.一种硅胶内增粘剂的制备方法，其特征在于，包括如下步骤：a.将含氢聚硅氧烷与含乙烯基硅烷按照nH:nVi=2:1-1.5的比例混合；b.加入步骤a总物料重量的9-20ppm的氯铂酸催化剂，控制反应温度在50-90摄氏度，反应1-2小时；c.降温至室温，加入含氢聚硅氧烷与含乙烯基硅烷总重量0.5-2%的抑制剂，得到硅胶内增粘剂成品。2.根据权利要求1所述的硅胶内增粘剂的制备方法，其特征在于，所述的含氢聚硅氧烷的含氢量为1.0-1.6%。3.根据权利要求1所述的硅胶内增粘剂的制备方法，其特征在于，所述的含乙烯基硅烷包括乙烯基三甲氧基硅烷、乙烯基三乙酰氧基硅烷、乙...
【专利技术属性】
技术研发人员：谢朝辉，黄胜，杨家昌，吴长林，邓军，焦冬生，张再成，
申请(专利权)人：惠州赛力珑新材料有限公司，
类型：发明
国别省市：广东,44