The invention discloses a hot rolled steel plate with excellent corrosion resistance of sulphuric acid and hydrochloric acid and a manufacturing method of the hot rolled steel plate. One aspect of the invention, provide hot rolled steel plate excellent corrosion resistance of the composite sulfuric acid and hydrochloric acid, by weight percent, including: C:0.05 ~ 0.1%, Mn:0.5 ~ 1.5%, P:0.02%, S:0.02%, Al:0.01 impurities below ~ 0.1%, Cu:0.2 ~ 0.6%, Sb:0.05 ~ 0.1%, Fe margin and the inevitable, from the surface to the inside along the thickness direction of 500nm concentration Cu and Sb, and the corrosion reduction of hydrochloric acid solution on 16.9 volume% sulfuric acid +0.35% by volume 2.0mg/cm
【技术实现步骤摘要】
【国外来华专利技术】硫酸及盐酸复合耐蚀性优异的热轧钢板及其制造方法
本专利技术涉及对于硫酸及盐酸的复合耐蚀性优异的热轧钢板及其制造方法，其能够优选适用于火力发电厂的脱硫设备、脱氮设备、预热器及其部件等材料。
技术介绍
含有燃烧煤炭或石油等化石燃料时所产生的亚硫酸气体及氯气的废气与水分反应并生成硫酸及盐酸，从而硫酸或硫酸-盐酸复合耐蚀钢用于硫酸或硫酸-盐酸复合腐蚀严重的火力发电厂的脱硫及脱氮设备或复合发电厂的管道及烟气换热器(GasGasHeater，GGH)的需要使用较厚的厚度的钢板的热元件(heatelement)材料等。众所周知，相比传统钢，硫酸-盐酸复合耐蚀钢为了在硫酸及盐酸复合气氛中延迟腐蚀速度，从而在钢中添加大量的铜(Cu)。与其他添加元素相比，铜(Cu)的延迟硫酸腐蚀速度的效果优异，但是，当添加大量铜时，在热轧时会引发钢板的裂纹等，因此开发了添加适当量的铜(Cu)的同时复合添加其他元素的钢(日本公开专利公报第1997-025536号、日本公开专利公报第1998-110237号、韩国公开专利公报第2009-0070249号等)。如上所述，在硫酸-盐酸复合耐蚀钢中，随着铜(C...
【技术保护点】
硫酸及盐酸复合耐蚀性优异的热轧钢板，其以重量％计，包含：C：0.05～0.1％、Mn：0.5～1.5％、P：0.02％以下、S：0.02％以下、Al：0.01～0.1％、Cu：0.2～0.6％、Sb：0.05～0.1％、余量Fe及不可避免的杂质，从表面到沿厚度方向的500nm以内浓缩有Cu及Sb，并且对16.9体积％的硫酸+0.35体积％的盐酸溶液的腐蚀减量为2.0mg/cm
【技术特征摘要】
【国外来华专利技术】1.硫酸及盐酸复合耐蚀性优异的热轧钢板，其以重量％计，包含：C：0.05～0.1％、Mn：0.5～1.5％、P：0.02％以下、S：0.02％以下、Al：0.01～0.1％、Cu：0.2～0.6％、Sb：0.05～0.1％、余量Fe及不可避免的杂质，从表面到沿厚度方向的500nm以内浓缩有Cu及Sb，并且对16.9体积％的硫酸+0.35体积％的盐酸溶液的腐蚀减量为2.0mg/cm2/小时以下。2.根据权利要求1所述的硫酸及盐酸复合耐蚀性优异的热轧钢板，其中，所述不可避免的杂质包含W、Mo、Co及Ni，其含量之合小于10ppm。3.根据权利要求1所述的硫酸及盐酸复合耐蚀性优异的热轧钢板，其特征在于，所述被浓缩的Cu及Sb在硫酸及盐酸腐蚀环境中形成包含Cu-Sb复合氧化物的氧化物层。4.根据权利要求3所述的硫酸及盐酸复合耐蚀性优异的热轧钢板，其特征在于，所述氧化物层以400～500nm的厚...
【专利技术属性】