The invention provides a coloring process for alumina material, which belongs to the field of metal surface treatment. The surface of aluminum workpiece coloring first mechanical polishing, electrolytic polishing and then treated with sulfuric acid oxidation surface aluminum workpiece, oxidation time in 30min, which is formed on the surface of a light film with thickness of 6 microns ~7 microns; the function of particles attached to the surface, then were stained with inorganic pigment. The products are polished, oxidizing, and can be attached to all kinds of inorganic pigments. And it has the health function of antibacterial, far infrared, or magnetic therapy.
【技术实现步骤摘要】
一种氧化铝材料的着色工艺
本专利技术涉及一种氧化铝材料的着色工艺,其属于金属表面处理领域。
技术介绍
由于我国铝资源丰富,铝制品的开发越来越得到人们的认可。如家用铝门窗,装饰材料等铝制品广泛受到人们的欢迎。但由于目前的铝制品色调单一化,功能单一,使铝材料的使用受到了局限。由于人们生活水平的提高,家居装修也更富丽堂皇,对颜色的要求在逐渐的加重,对功能的要求也逐渐的重视,带有功能性的多色金属材料更加受到人们的欢迎。
技术实现思路
鉴于已有技术存在的缺陷,本专利技术提供一种氧化铝材料的着色工艺,解决铝制品色彩单一和功能性的问题。为实现上述目的,本专利技术所采用的技术方案是一种氧化铝材料的着色工艺,铝制品工件着色的表面先进行机械抛光,电解抛光处理后再用再将铝制品工件表面进行硫酸液氧化,氧化的时间要在30min,使表面形成有光亮的氧化膜,其厚度在6微米~7微米;采用功能物质颗粒附着在其表面,然后在用无机颜料进行染色。所述功能物质颗粒为二氧化钛,二氧化钛通过紫外线的作用,在表面生成活性氧类,活性氧显示出抗菌作用。所述功能物质颗粒为远红外粉或永磁粉,或者远红外粉和永磁粉的混合物,混合比例为1:1~2:1,通过自身辐射作用,在表面形成辐射区。采用上述方案后,与现有技术相比具有以下有益效果:产品经过抛光,氧化,可以附着而各种无机颜料色。并且具有抗菌,远红外或磁疗的保健功能。具体实施方式为了达到铝制品的光亮度和逼真的色彩,在着色的表面必须先进行机械抛光,电解抛光等前道处理后再用硫酸液氧化,氧化膜的厚度至少在6微米以上,因此氧化的时间要在30min。经过氧化后的铝材料用可溶性还原颜 ...
【技术保护点】
一种氧化铝材料的着色工艺,其特征在于:铝制品工件着色的表面先进行机械抛光,电解抛光处理后再用再将铝制品工件表面进行硫酸液氧化,氧化的时间要在 30min, 使表面形成有光亮的氧化膜,其厚度在 6 微米 ~7 微米 ;采用功能物质颗粒附着在其表面,然后在用染料进行染色。
【技术特征摘要】
1.一种氧化铝材料的着色工艺,其特征在于:铝制品工件着色的表面先进行机械抛光,电解抛光处理后再用再将铝制品工件表面进行硫酸液氧化,氧化的时间要在30min,使表面形成有光亮的氧化膜,其厚度在6微米~7微米;采用功能物质颗粒附着在其表面,然后在用染料进行染色。2.根据权利要求1所述的一种氧化铝材料的着色...