本发明专利技术公开一种溶液法制备金属钴的方法，其是将四水合醋酸钴溶于乙二醇和去离子水组成的混合液中，将溶液转移至高压反应釜中，并将密闭的反应釜放到提前预热的烘箱内，然后烘箱温度按照2～5℃/分钟的升温速度逐渐升温至200℃～210℃，并在该温度下保温20～24小时，待反应结束反应釜冷却至室温，混合液经过滤、洗涤、干燥后，即得金属钴。本发明专利技术工艺简单、成本低，最终获得的产品纯度高。

A solution method for the preparation of cobalt metal

The invention discloses a method for solution preparation of cobalt metal, cobalt acetate is four hydrated dissolved in ethylene glycol mixed solution and deionized water in the solution will be transferred to the high-pressure reaction kettle, and a sealed reaction kettle in the oven preheating, and oven temperature according to 2 to 5 DEG C the heating rate per minute gradually warming up to 200 to 210 DEG C, and the temperature of 20 to 24 hours after the reaction, the reaction kettle is cooled to room temperature, the mixture was filtered, washed and dried, the metal cobalt. The invention has the advantages of simple process, low cost, and high purity of the final product.

【技术实现步骤摘要】
一种溶液法制备金属钴的方法
本专利技术涉及材料粉体的制备领域，具体涉及一种溶液法制备金属钴的方法。
技术介绍
金属钴是一种重要的功能性材料，它具有优异的理化性能,在许多领域有着重要的应用。金属钴具有优异的磁学性能，因此它在高密度存储介质和磁记忆装置领域有着广泛的应用。此外金属钴也被广泛地应用于高强度耐高温合金、工业催化、功能陶瓷、电池等诸多领域。目前，制备金属钴的方法有许多种，如氧化物还原法、电解法、液相还原法等。氧化物还原法是将钴的氧化物，用氢气和一氧化碳等还原性物质还原得到金属钴。电解法是通过电化学还原的方法来获得金属钴,电解法制备出金属钴微观形貌多为枝状或针状。液相还原法是将钴的固体化合物分散在液体中，液体通常为多元醇(如乙二醇等)和液相还原剂的混合液，然后将其加热到一定温度，从而使化合物发生还原反应获得金属钴。相比于其他方法，液相还原法生产工艺简单易操作,生产原料形态多种多样,产品粒度可以有效调节控制。但常规的液相还原法的反应溶液体系中往往需要加入多种化学试剂才能完成，成本高，产品纯度不高，且操作复杂。
技术实现思路
针对现有技术中的不足，本专利技术提出一种溶液法制备金属钴的方法本文档来自技高网...

【技术保护点】
一种溶液法制备金属钴的方法，其特征在于，其包括如下具体步骤：(1)将四水合醋酸钴溶于乙二醇和去离子水组成的混合液中，搅拌使四水合醋酸钴充分溶解于混合液中。(2)将步骤(1)中的溶液转移至高压反应釜中，填充率为60～75vol％，并将密闭的反应釜放到提前预热到140～150℃的烘箱内，烘箱温度按照2～5℃/分钟的升温速度逐渐升温至200℃～210℃，并在该温度下保温20～24小时，待反应结束反应釜冷却至室温，混合液经过滤、洗涤、干燥后，即得金属钴。

【技术特征摘要】
1.一种溶液法制备金属钴的方法，其特征在于，其包括如下具体步骤：(1)将四水合醋酸钴溶于乙二醇和去离子水组成的混合液中，搅拌使四水合醋酸钴充分溶解于混合液中。(2)将步骤(1)中的溶液转移至高压反应釜中，填充率为60～75vol％，并将密闭的反应釜放到提前预热到140～150℃的烘箱内，烘箱温度按照2～5℃/分钟的升温速度逐渐升温至200...