The noble metal catalyst provided by the invention comprises a shell powder coating and noble metal nano particles, can catalyze the oxygen in the air and indoor formaldehyde, benzene, ammonia, TVOC and other indoor harmful gases accelerate the oxidation reduction, and decomposition of harmful gases into harmless substances such as carbon dioxide and water; at the same time, noble metal nano particles of catalyst in the process of effect of catalytic oxygen and harmful gas, does not participate in any chemical reaction, so nano particles will not produce long time consumption, can continue to play a role of indoor air purification. In addition, the invention also provides a preparation method of the above - mentioned noble metal catalyst.
【技术实现步骤摘要】
贵金属催化剂的制备方法及贵金属催化剂
本专利技术涉及催化剂制备
，特别是涉及一种贵金属催化剂及其制备方法。
技术介绍
纳米贵金属催化剂因其巨大的比表面积在催化反应中表现出独特的性能，其制备与应用已被广泛报道。纳米贵金属催化剂的制备通常是在高分子稳定剂，如聚乙烯基吡咯烷酮(PVP)、聚乙二醇(PEG)、聚-N-异丙基丙烯酰胺等存在下，使用醇类、NaBH4等还原剂，在溶液中还原贵金属盐类得到分散在溶剂中的贵金属纳米粒子。为了得到稳定的纳米金属粒子，往往还需辅助加入长链胺或者水溶性膦。例如，中国专利CN1058919公开了一种纳米金属粒子的制备方法，将贵金属络合物或者金属盐的水溶液与稳定剂十二烷基苯磺酸钠水溶液混合，加入三苯基磷单磺酸钠或三苯基磷三磺酸钠稳定剂，另外还需要低温和高压氢气处理才能获得粒径均匀分布的纳米金属粒子。中国专利CN101045206公开了一种用于费托合成的纳米金属催化剂，该催化剂使用PVP或者[BVIMPVP]Cl(一种共聚高分子，参见J.Am.Chem.Soc.2005，127，9694-9695)作为保护剂，液体介质为水、乙醇、环己烷等，...
【技术保护点】
一种贵金属催化剂的制备方法，其特征在于，包括下述方法：将贵金属的酸性水溶液与溶有二十二烷基三甲基溴化铵溶液的去离子水溶液搅拌混合，得到混合溶液；将所述混合液滴入氢硼化钠水溶液，再进行搅拌后静置待混合溶液与去离子水分层；萃取上层的的纳米贵金属颗粒的水溶液，并将所述纳米贵金属颗粒的水溶液烘干处理，得到贵金属纳米颗粒。
【技术特征摘要】
1.一种贵金属催化剂的制备方法，其特征在于，包括下述方法：将贵金属的酸性水溶液与溶有二十二烷基三甲基溴化铵溶液的去离子水溶液搅拌混合，得到混合溶液；将所述混合液滴入氢硼化钠水溶液，再进行搅拌后静置待混合溶液与去离子水分层；萃取上层的的纳米贵金属颗粒的水溶液，并将所述纳米贵金属颗粒的水溶液烘干处理，得到贵金属纳米颗粒。2.根据权利要求1所述的贵金属催化剂，其特征在于，在将贵金属的酸性水溶液与溶有二十二烷基三甲基溴化铵溶液的去离子水溶液混合，得到混合溶液的步骤中，所述贵金属的酸性水溶液为金氯酸水溶液。3.根据权利要求1所述的贵金属催化剂，其特征在于，在将贵金属的酸性水溶液与溶有二十二烷基三甲基溴化铵溶液的去离子水溶液混合，得到混合溶液的步骤中，所述贵金属的酸性水溶液与二十二烷基三甲基溴化铵的体积质量比为60～85ml：0.48...
【专利技术属性】
技术研发人员：黄皆美，
申请(专利权)人：深圳砺剑超能材料有限公司，
类型：发明
国别省市：广东,44