一种铂金凹凸棒土纳米负载催化剂及其制备方法和应用技术

本发明专利技术公开了一种铂金凹凸棒土纳米负载催化剂及其制备方法和应用。所述催化剂载体为凹凸棒土，活性组分是铂金，其平均粒径约为3～8纳米，催化剂中铂的质量分数为1.3～2.5％，金的质量分数为0.5～2％。本发明专利技术的铂金凹凸棒土纳米负载催化剂具有清洁环保而有方便的特点，并且本发明专利技术的铂金凹凸棒土纳米负载催化剂对硝基苯酚还原为氨基苯酚具有优异催化性能。

Platinum attapulgite nano load catalyst and its preparation method and Application

The invention discloses a platinum attapulgite nano load catalyst, and its preparation method and application. The catalyst carrier is attapulgite, the active component is platinum, the average particle size is about 3~8 nm, the mass fraction of platinum in the catalyst is 1.3 to 2.5%, and the mass fraction of the gold is 0.5 to 2%. The platinum attapulgite nano loading catalyst has the advantages of cleanness, environmental protection and convenience, and the platinum attapulgite nano loading catalyst of the invention reduces the p-nitrophenol to p-aminophenol, and has excellent catalytic performance.

【技术实现步骤摘要】
一种铂金凹凸棒土纳米负载催化剂及其制备方法和应用
本专利技术涉及工业催化
，尤其涉及一种铂金凹凸棒土纳米负载催化剂及其制备方法和应用。
技术介绍
近几十年来，负载型纳米催化剂已得到广泛应用。关于金属和载体间的相互作用的研究报道日益增多。众所周知，金属和载体间特殊的相互作用会影响催化剂的表面性能，进而影响它的催化活性。比如，在Al2O3载体担载金属钴的过程中钴离子会迁移到Al2O3的晶格中形成CoAl2O4化合物。铁的氧化物和过渡金属氧化物或其碳酸盐发生固-固作用形成相应的铁氧体氧化物CoFe2O4。金纳米微粒具有高表面能，容易发生团聚。若将金纳米微粒负载在载体上可有效地阻止其团聚，从而提高催化剂的催化活性。凹凸棒土是一种具纤维纹理层链状过渡结构的含水富镁硅酸盐为主的粘土矿，在矿物学上属于海泡石族，其化学式为：Mg5(H2O)4[Si4O10]2(OH)2·4H2O，在凹凸棒土晶体中，一部分的Si4+被Mg2+和Al3+所替代且缺少正电荷，表现出一定的电负性，它具有独特的链式结构，表现出不同寻常的吸附性能。氨基苯酚是一种用途广泛的有机合成中间体，通常用于制备各种止痛药物(如扑热息本文档来自技高网...

【技术保护点】
一种铂金凹凸棒土纳米负载催化剂，其特征在于：所述催化剂载体为凹凸棒土，活性组分是铂金，其平均粒径约为3～8纳米，催化剂中铂的质量分数为1.3～2.5％，金的质量分数为0.5～2％。

【技术特征摘要】
1.一种铂金凹凸棒土纳米负载催化剂，其特征在于：所述催化剂载体为凹凸棒土，活性组分是铂金，其平均粒径约为3～8纳米，催化剂中铂的质量分数为1.3～2.5％，金的质量分数为0.5～2％。2.一种制备如权利要求1所述的铂金凹凸棒土纳米负载催化剂的方法，其特征在于：所述方法的具体步骤如下：(1)载体的处理用200～300目筛筛取粉碎后的凹凸棒土，加入酸溶液，加热回流4小时后，抽滤，清洗至pH为5～10，干燥至恒重，备用；(2)PtAu溶胶的制备向H2PtCl6、HAuCl4溶液加入稳定剂，H2PtCl6、HAuCl4与稳定剂的摩尔比为2:1:15，搅拌均匀后滴加还原剂溶液，还原剂与稳定剂的摩尔比为1:1，继续搅拌2时间，制得稳定铂金溶胶；(3)PtAu/ATP纳米催化剂...

【专利技术属性】
技术研发人员：戴兢陶，杨子健，孙远旭，房月，吴振，胡朝俊，杨锦明，
申请(专利权)人：盐城锦明药业有限公司，
类型：发明
国别省市：江苏,32