The invention discloses a building materials of a high strength anti cracking porous insulation brick, by weight, the high intensity of porous insulating brick comprises the following components: Perlite 50~100, polyvinyl fluoride 35~85, lithium bentonite 10~40, calcined kaolin 5~25, calcium carbonate, 3~10 sepiolite 5~10. The long, wide and high length ratio of the high - strength anti - crack insulating brick is 10~20:5~10:2~5. Compared with the traditional expanded perlite insulation brick, the high strength anti cracking porous insulation brick has better thermal insulation performance, and its mechanical strength and water resistance have been further improved. It is a worthy thermal insulation material.
【技术实现步骤摘要】
一种高强度抗裂多孔保温砖
本专利技术属于建筑材料领域，具体涉及一种高强度抗裂多孔保温砖。
技术介绍
工业化的进程给我们带来了社会的进步、生产力的大幅提高，但同时也引发了一系列的能源危机。随着对能源开采的逐年加剧，地球上的化石、燃料等不可再生资源已经渐渐枯竭，能源危机的警钟已经敲响。近几年来，能源问题引起了世界各国越来越多的关注，并被列入了人类面临的四大生存问题之一。各类热工设备及建筑的保温绝热，是节能的重要措施。保温绝热材料是节能的物质基础，性能优良的保温绝热材料和良好的保温技术，在工业保温中往往可起到事半功倍的效果。传统膨胀珍珠岩保温材料是以膨胀珍珠岩为骨料，聚氟乙烯、磷酸盐等为粘结剂在高温下焙烧而成，或者通过添加水泥等固化剂在60～120℃条件下静置固化得到。传统保温材料的保温效果、机械强度和防水性都可以进一步的提高。
技术实现思路
本专利技术提供了一种高强度抗裂多孔保温砖及其制备方法。一种高强度抗裂多孔保温砖，按重量计，所述高强度抗裂多孔保温砖包括下述组分：膨胀珍珠岩50～100份、聚氟乙烯35～85份、锂基膨润土10～40份、煅烧高岭土5～25份、碳酸钙3～1...
【技术保护点】
一种高强度抗裂多孔保温砖，其特征在于，按重量计，所述高强度抗裂多孔保温砖包括下述组分：膨胀珍珠岩50～100份、聚氟乙烯35～85份、锂基膨润土10～40份、煅烧高岭土5～25份、碳酸钙3～10份、海泡石5～10份。
【技术特征摘要】
1.一种高强度抗裂多孔保温砖，其特征在于，按重量计，所述高强度抗裂多孔保温砖包括下述组分：膨胀珍珠岩50～100份、聚氟乙烯35～85份、锂基膨润土10～40份、煅烧高岭土5～25份、碳酸钙3～10份、海泡石5～10份。2.根据权利要求1所述的一种高强度抗裂多孔保温砖，其特征在于，按重量计，所述高强度抗裂多孔保温砖包括下述组分：膨胀珍珠岩50～60份、聚氟乙烯35～55份、锂基膨润土15～20份、煅烧高岭土5～10份、碳酸钙3～6份、海泡石5～10份。3.根据权利要求1所述的一种高强度抗裂多孔保温砖，其特征在于，所述高强度抗裂多孔保温砖的生产工艺包括以下步骤：（1）按照所述配比称取膨胀珍珠岩、锂基膨润土、煅烧高岭土、碳酸钙、海泡石，...