The present invention provides a toughened epoxy resin mold material and its preparation method, the mold materials include: E44 epoxy resin, polysulfide rubber, thermoplastic polyurethane, polycarbonate, polyamide, graphite, short glass fiber, toluene, butyl alcohol, methyl methacrylate, curing agent,. Plasticizer, stabilizer, lubricant, emulsifier. The preparation method is that firstly the E44 epoxy resin, polycarbonate, polyamide, graphite, short glass fiber, PMMA mixed, ball milling, and the mixture was added to the mixture of toluene and n-butanol, stirring, adding polysulfide rubber, thermoplastic polyurethane, curing agent, plasticizer agent, stabilizer, lubricant and emulsifier, ultrasonic dispersion, the mixture is cured, you can. The epoxy resin mould material prepared by the invention has good impact resistance, high compressive strength and fast curing speed.
【技术实现步骤摘要】
一种增韧环氧树脂模具材料及其制备方法
本专利技术属于树脂模具材料
，具体涉及一种增韧环氧树脂模具材料及其制备方法。
技术介绍
树脂基快速模具材料是近年来发展起来的一种新型功能材料，具有较高的形状稳定性、刚性、冲击韧性、硬度以及良好的加工性能、耐热性、表面特性和耐腐蚀性等，相对质量较轻，又便于改型或修理，且速度更快、成本更低，不但能缩短模具的制作时间，降低模具制作成本，还能提高模具加工精度。在玩具、建筑、汽车、化工等多种领域得到广泛应用，可以说树脂基快速模具技术的出现有力地推动了模具工业的快速发展。树脂基快速模具材料必须满足：能在常温、常压下进行浇注；流动性好，容易充满各种型腔；固化时生成低沸点物或气体很少，且固化时间短；化学反应平缓，体积收缩较小，不易产生缩孔及残余内应力。环氧树脂是最常用的模具材料之一，其固化后交联成不溶树脂固化物，具有优异的力学性能、加工性能、耐化学药品性、电气绝缘性、尺寸稳定性、低吸水率、黏结性、耐腐蚀性等。但是环氧树脂脆性高，耐温低，影响了使用寿命，因此，对环氧树脂模具材料的增韧改性就显得十分必要。
技术实现思路
本专利技术的目的是提供一...
【技术保护点】
一种增韧环氧树脂模具材料，其特征在于：原料以重量份计包括：E44环氧树脂100份，聚硫橡胶15‑23份，热塑性聚氨酯弹性体3‑6份，聚碳酸酯2‑4份，低分子量聚酰胺1‑3份，石墨20‑30份，短切玻璃纤维3‑5份，甲苯4‑7份，正丁醇3‑8份，聚甲基丙烯酸甲酯2‑5份，固化剂8‑12份，增塑剂2‑6份，稳定剂1‑3份，润滑剂1‑3份，乳化剂0.8‑1.5份。
【技术特征摘要】
1.一种增韧环氧树脂模具材料，其特征在于：原料以重量份计包括：E44环氧树脂100份，聚硫橡胶15-23份，热塑性聚氨酯弹性体3-6份，聚碳酸酯2-4份，低分子量聚酰胺1-3份，石墨20-30份，短切玻璃纤维3-5份，甲苯4-7份，正丁醇3-8份，聚甲基丙烯酸甲酯2-5份，固化剂8-12份，增塑剂2-6份，稳定剂1-3份，润滑剂1-3份，乳化剂0.8-1.5份。2.根据权利要求1所述的增韧环氧树脂模具材料，其特征在于：所述增塑剂为邻苯二甲酸二辛酯。3.根据权利要求1所述的增韧环氧树脂模具材料，其特征在于：所述稳定剂为有机锡类稳定剂。4.根据权利要求1所述的增韧环氧树脂模具材料，其特征在...
【专利技术属性】
技术研发人员：刘浩，张君，张欢芬，