利用羊毛角蛋白制备纳米银的方法技术
Preparation of silver nanoparticles from wool keratin
The invention relates to a method for preparing wool keratin using silver nanoparticles, which comprises the following steps: adding wool to the molten urea, heat treatment, after dialysis, get wool keratin solution with alkali; wool keratin solution is adjusted to pH 9 12, which added to the aqueous solution of silver in the 80, the reaction liquid reaction 98 DEG C, obtained silver nanoparticles. The method is simple, easy to control, wool keratin by urea melt extraction as prepared nano silver agent and stabilizer for the reduction, exemption and other non eco friendly reductant and polymer stabilizer and dispersant added, can be directly applied to the obtained nano silver biological materials, composite materials, textile functional finishing agent other fields; the obtained silver nanoparticles with uniform particle size, particle size, dispersion and stability.
【技术实现步骤摘要】
利用羊毛角蛋白制备纳米银的方法
本专利技术涉及纳米材料制备
，尤其涉及一种利用羊毛角蛋白制备纳米银的方法。
技术介绍
我国是毛纺工业大国，羊毛品种和资源极其丰富，但因受羊毛品质、饲养管理、纺织技术等因素的制约，每年都会产生大量的被废弃的羊毛短纤维和粗纤维。废弃的羊毛主要来自于以下三个方面：一是部分羊品种以及不良的生活环境所致的品质差的羊毛，二是在饲养管理方面因剪毛或者其它加工操作不当而导致产生了大量的可纺性差的羊毛短纤维，这些短纤维基本无纺织价值；三是养殖场、屠宰场、制革厂在生产加工过程中产生的大量废弃羊毛。这些废弃的羊毛，如果被随意丢弃，不仅是一种资源的浪费，而且也污染了环境。废弃的羊毛含有丰富的角蛋白，从废弃的羊毛中将角蛋白提取出来、并加以利用无疑是一种变废为宝、绿色环保的生产加工方式，对环境生态和经济的可持续发展具有重要的意义。从废弃羊毛中提取的羊毛角蛋白可以应用于多个领域，例如，可用作纺织品功能性整理剂、复合材料、吸附剂、生物医用材料等。从羊毛中提取角蛋白的方法一般有氧化法和还原法，氧化法会引起羊毛纤维二硫键和肽键的同时断键，因而所提取的角蛋白分子质...
【技术保护点】
一种利用羊毛角蛋白制备纳米银的方法，其特征在于，包括以下步骤：(1)向熔融的尿素中加入羊毛，热处理、透析后，得到羊毛角蛋白水溶液；(2)用碱将所述羊毛角蛋白水溶液的pH调节至9‑12，向其中加入银盐的水溶液，将反应液在80‑98℃下反应，得到所述纳米银。
【技术特征摘要】
1.一种利用羊毛角蛋白制备纳米银的方法，其特征在于，包括以下步骤：(1)向熔融的尿素中加入羊毛，热处理、透析后，得到羊毛角蛋白水溶液；(2)用碱将所述羊毛角蛋白水溶液的pH调节至9-12，向其中加入银盐的水溶液，将反应液在80-98℃下反应，得到所述纳米银。2.根据权利要求1所述的利用羊毛角蛋白制备纳米银的方法，其特征在于：在步骤(1)中，所述尿素与羊毛的质量比为100:10-50:10。3.根据权利要求1所述的利用羊毛角蛋白制备纳米银的方法，其特征在于：在步骤(2)中，所述反应液中羊毛角蛋白的浓度为0.0057-0....
【专利技术属性】
技术研发人员：王冬悦，李冰艳，杨旭红，唐人成，
申请(专利权)人：南通纺织丝绸产业技术研究院，
类型：发明
国别省市：江苏,32